Electronics Forum | Tue Apr 06 20:28:41 EDT 1999 | Scott McKee
| I need help in finding solder paste measuring equipment. | Height, length, width, area, volume after printing (off line): 1. Cyberoptics:1-800-745-6315 www.cyberoptics.com 2. Manix Manufacturing 1-215-953-9797 3. Theta Group 1-205-650-0535 4.
Electronics Forum | Tue Feb 22 11:53:16 EST 2000 | JAX
Sal, To answer your first statement; Yes, you can cure paste and reflow solder using one profile. Question on your second statement; Are you talking about running passive side glue, flipping it over, running active side solder, and then putting the
Electronics Forum | Tue Feb 22 11:53:16 EST 2000 | JAX
Sal, To answer your first statement; Yes, you can cure paste and reflow solder using one profile. Question on your second statement; Are you talking about running passive side glue, flipping it over, running active side solder, and then putting the
Electronics Forum | Fri Feb 25 02:30:32 EST 2011 | pkannan
Dstadem, Thanks for bringing your in valuable experience with the J STD 005 " Requirements of Solder Paste". I fully agree with you that the Solder Paste can be qualified for shelf life by doing simple viscosity test and visual inspection for coal
Electronics Forum | Wed May 12 12:22:38 EDT 2004 | solderpro
I agree with the guy about cars, boats, ect... ok, I like as some have said without a doubt, DEK top of the line.... pick and place, love siemens but software is not user friendly, myself, JUKI all the way, great equipment, great software, that mean
Electronics Forum | Mon Nov 01 16:41:58 EST 1999 | Robert Culpepper
Hello Mark, I can�t provide any hands on feedback with 0402 packages but we are using a no clean process with 0603 devices. Here are some parameters which will affect solder balling. Stencil thickness, aperture size, paste viscosity, snap off and bot
Electronics Forum | Fri Jul 09 19:35:05 EDT 1999 | Earl Moon
| Hi Carol- | What you are asking for can be done. Variables you must account for include the paste viscosity, dispensing head speed, dispenser height relative to board surface, and needle size. You can use most any semi-automated system such as Ca
Electronics Forum | Thu Jul 26 13:17:45 EDT 2001 | Hussman
Most solder paste manufacturers will take a reasonable amount of paste back, just so they won't loose your business due to bad paste. But if you're asking to ask to ask - separated paste from flux is not a bad thing if the jar was never opened. Pas
Electronics Forum | Thu Jun 25 21:13:11 EDT 1998 | Phillip Hunter
| looking for help with fine-pitch printing for what would be the best settings for printing speed, squeegee pressure, seperation speed. | thanks for you time Print speed is determined by your aperture dimensions, paste viscosity type of blade (metal
Electronics Forum | Tue May 02 05:59:28 EDT 2006 | davef
We agree with Ken's points about off contact / screen versus stencil, but this DHolt is talking stencil [regardless of what is typed about screens]. Comments are: * On "smears under the stencil": smearing happens. It makes us wonder about the frequ