Electronics Forum | Thu Jun 04 09:53:31 EDT 1998 | Dave F
| I have gold fingers that I want to mask when running over the wave without pallets. They're on the leading edge of the board. I recall seeing rubber boots that slid onto the fingers to mask them. Pop 'em on before the wave; pop' em off after and
Electronics Forum | Thu Jun 04 20:52:57 EDT 1998 | D.Lange
| | I have gold fingers that I want to mask when running over the wave without pallets. They're on the leading edge of the board. I recall seeing rubber boots that slid onto the fingers to mask them. Pop 'em on before the wave; pop' em off after a
Electronics Forum | Wed Jun 30 10:37:11 EDT 1999 | Boca
We are wave soldering some fabs with a lot of unmasked trace area along the edges. The trace area is solid copper covered with tin / lead, no masking, no components along the edges, same on solder side and component side (goofy board design). Inste
Electronics Forum | Wed Jun 30 17:58:01 EDT 1999 | Boca
| My guess would be trapped flux continuing to be active after soldering. Is the tarnish there immediately after exiting the machine? Do you remove the mask and wash right away? If the solder is reflowing under the mask on the component side it wo
Electronics Forum | Fri Jul 02 09:54:02 EDT 1999 | John Thorup
| | | | We are wave soldering some fabs with a lot of unmasked trace area along the edges. The trace area is solid copper covered with tin / lead, no masking, no components along the edges, same on solder side and component side (goofy board design)
Electronics Forum | Fri Jul 02 10:06:17 EDT 1999 | John Thorup
| | | | We are wave soldering some fabs with a lot of unmasked trace area along the edges. The trace area is solid copper covered with tin / lead, no masking, no components along the edges, same on solder side and component side (goofy board design)
Electronics Forum | Thu Apr 15 09:45:34 EDT 1999 | Terry Keen
| | We process both tin/lead plated boards and gold plated boards in our surface mount group. I have used Sn62/Pb36/Ag2 solder paste on all gold plated boards to help prevent gold scavaging. To reduce the amount of different solder pastes we have t
Electronics Forum | Thu Jul 01 14:47:10 EDT 1999 | Tony
| | | My guess would be trapped flux continuing to be active after soldering. Is the tarnish there immediately after exiting the machine? Do you remove the mask and wash right away? If the solder is reflowing under the mask on the component side
Electronics Forum | Wed Jun 30 12:14:40 EDT 1999 | John Thorup
| | We are wave soldering some fabs with a lot of unmasked trace area along the edges. The trace area is solid copper covered with tin / lead, no masking, no components along the edges, same on solder side and component side (goofy board design). I
Electronics Forum | Fri Jul 02 05:28:13 EDT 1999 | Vinesh gandhi
| | | We are wave soldering some fabs with a lot of unmasked trace area along the edges. The trace area is solid copper covered with tin / lead, no masking, no components along the edges, same on solder side and component side (goofy board design).