Electronics Forum | Fri Apr 10 20:35:59 EDT 1998 | Steve Gregory
| | We are having a bridging problem with SOIC 14,16 and 20 pin devices during flow solder of the bottom side of our boards. This bridging occurs about half way up the lead between the board and the body of the IC. The chip parts are no problem. T
Electronics Forum | Mon Apr 13 08:42:32 EDT 1998 | Bob Silveri
| | | | We are having a bridging problem with SOIC 14,16 and 20 pin devices during flow solder of the bottom side of our boards. This bridging occurs about half way up the lead between the board and the body of the IC. The chip parts are no proble
Electronics Forum | Sun Oct 01 23:58:55 EDT 2000 | stuartfd
Dear forum types, 1st timer so be good. I have a customer in China using Coates soldermask that in its self is not a problem. The problem is the flux their using, I think,it appears to have a vary high viscosity. The problem they have laid at my door
Electronics Forum | Thu Jun 25 21:13:11 EDT 1998 | Phillip Hunter
| looking for help with fine-pitch printing for what would be the best settings for printing speed, squeegee pressure, seperation speed. | thanks for you time Print speed is determined by your aperture dimensions, paste viscosity type of blade (metal
Electronics Forum | Thu Nov 10 14:58:16 EST 2005 | Karkanov
Hi, I had a question from our ISO guy asking me how I know that the paste we use is in good condition? The problem is that he saw our operator put some old paste back in a empty jar to reuse it the next day. So his question is how do you know the
Electronics Forum | Wed Apr 19 16:43:05 EDT 2006 | samir
Silicone-based coatings "repel" most foreign,non-compatible materials like peelable solder mask, and rubber or vinyl boots. The result is, uncured material around the vicinity of where the boot was. Trust me. Been there and done that. As a rookie
Electronics Forum | Wed Feb 23 03:22:47 EST 2011 | pkannan
(Corrected the Subject line - sorry for Spelling ) You are very right. There are 2 major factors 1) There is going to be Flux separation. This is basically due to fact that metal particles are heavier than the Flux vehicle system, and due to gravity
Electronics Forum | Wed Aug 01 15:18:40 EDT 2018 | dleeper
One option might be to convert the coil to through hole and use intrusive reflow AKA pin in paste. the coil leads would have to be formed perpendicular to the board instead of parallel. you would have through holes instead of SMT pads, but you would
Electronics Forum | Fri Oct 05 15:35:19 EDT 2018 | davef
Paste sticking to squeegee: * Squeegee is heavily magnetized * Some pastes stick more than ... * Plastic squeegees stick more than metal * Old metal squeegees stick more than new * Paste needs to be worked * Paste needs to be at room temperatur
Electronics Forum | Wed Nov 21 12:29:52 EST 2001 | mparker
Now that we know where you've been and what you wish to accomplish next, I can still give you some suggestions. 1. Get IPC-7912. Use it to evaluate your CM's. Especially if you have multiple contractors supplying like products. You will quickly see