Electronics Forum | Wed May 12 17:37:08 EDT 1999 | Timothy O'Neill
| I am looking for anyone who has converted over to VOC Free flux. I need some info on any problems, etc. that you might have had. | | Please E-mail me at wes.ruggles@vickers-systems.com or call at (513) 494-5229 | | Thanks | Wes Ruggles | Hi Wes
Electronics Forum | Tue Sep 22 12:58:18 EDT 1998 | Chyrs
| How can I solve the small solder ball in the N2 W/S ? | The Oxygen level is 10000~20000ppm & no-clean flux. Yuen, Sorry I an't got an answer, just more questions. 1-2% O2 in your wave solder - are you running membrane generated nitrogen? I don't
Electronics Forum | Fri Jun 22 05:03:29 EDT 2001 | wbu
no - can it be left uncleaned on the board? ---> for many applications yes says our supplier and many companies do ( techi over there) - are our products specified for conditions that we and our customers can live with that? ---> well, at first
Electronics Forum | Fri Dec 17 08:29:18 EST 1999 | Wolfgang Busko
Hi Chuck, let�s say it the other way round. We use noclean since I can�t even remember without nitrogen and all of our subcons do with no known problems. The processes are adapted to it and no complaints are heard up to now. That is related to our pr
Electronics Forum | Thu Oct 14 08:01:48 EDT 1999 | JohnW
Gee Dave That's the first time I've ever seen myself listed for a quote! Brian, what your saying is on the whole right, on the surface of it the mask, as long as it's cured properlay shouldn't make a difference but I have to say that I've found so f
Electronics Forum | Wed Sep 08 17:31:58 EDT 1999 | Earl Moon
| I am wave soldering a single sided through hole PCB array with (6) .040" round diameter pins that sit .5" off the PCB, and .080" apart. The problem being experienced is that solderballs are appearing on the end of the pins. I have tried decreasin
Electronics Forum | Thu Aug 05 10:55:09 EDT 1999 | Wolfgang Busko
| | | | | | Hello, | If you are using no-clean and they are entrapped in the flux it is also IPC accepted but i havent found a customer yet who agrees with that. Im sure you have checked your profile. I had the same problem with chip components but
Electronics Forum | Wed May 19 11:50:32 EDT 1999 | Chris Nuttall
We care currently running into problems during our plug via process: At the moment we plug prior to soldermask (LPISM) using epoxy resin - plugging takes place from the component side - however we are seeing solderballs after solder level.This is cau
Electronics Forum | Thu Apr 29 17:38:47 EDT 1999 | JohnW
Ok folk's has anyone used Alpha Metal's UP78 solder paste ? Our place is looking to move to that as the way to go, getting rid of the Hereaus 362's and Alpha 737's of the current set up. My question's are really : how is the printability of the pas
Electronics Forum | Thu Oct 01 11:40:17 EDT 1998 | Justin Medernach
Are there anyone who can give me the answer about solder ball problem? | We have 12 layer PCB and double sided PCB. After one side reflow soldering We found lots of solder ball under the PCB. The solder ball was coming out from via hole. | So