Electronics Forum | Thu Jul 26 22:52:47 EDT 2001 | davef
GT 8 years ago every board saw "touchup". Touch was done to fix boards to conform to A-610. Now A-610 allows less than complete hole fill. Our operators were totally freaking nuts about touching boards. They touched each others touch and on and o
Electronics Forum | Mon Apr 13 12:11:41 EDT 1998 | Justin Medernach
| | | I would like to invite everyone to share/discuss | | information/knowledge/experience they have with | | the req's that are assumed to be valid for the | | temperature/time relation in the process of reflow | | soldering Pin In Paste, Intrusiv
Electronics Forum | Mon Mar 12 11:27:35 EDT 2007 | coop
I am not using a solder pallet, I don't think the problem is contamination related, because these parts are on some of our other assemblies, and they're being waved with no problems. The problem seems to be mainly on our panelized boards for some rea
Electronics Forum | Mon Jun 07 10:52:04 EDT 1999 | Brian Wycoff
| | | | Where I can find some informations about repairing of SMT boards? | | | | | | | | Thanks | | | | | | | | Marcos | | | | | | | A first place to start is IPC's 7711 and 7721 encompasing repair, modification, and rework procedures. | | | |
Electronics Forum | Fri Jun 04 15:04:16 EDT 1999 | Earl Moon
| I'm encountering a new problem at my new company that I haven't encountered before in my past life - and that's Wave Soldering VIA holes. | | We've been getting a rash of defects that we call in this company, "insufficient solder in VIA hole." The
Electronics Forum | Mon Jan 28 19:58:02 EST 2002 | davef
Thanks for cutting me some slack on that metric thang, pardner. ;-) ANALYSIS: What??? The 5DX is useful for something!!! Shut ma mouth!!! [Don't you say a thing. I think I know what you're thinking.] FOAM FLUXERS: Your correct, not having a fo
Electronics Forum | Fri Jun 04 03:03:52 EDT 1999 | Scott B
| I'm encountering a new problem at my new company that I haven't encountered before in my past life - and that's Wave Soldering VIA holes. | | We've been getting a rash of defects that we call in this company, "insufficient solder in VIA hole." The
Electronics Forum | Sun Feb 06 07:49:16 EST 2000 | Dave F
Casimir: A comment and a couple questions: * Have you considered a machine that forms component leads to "self-clinch?" With this forming components snap into hole in the boards with the proper finished lead length and requires not trimming after
Electronics Forum | Thu May 25 08:47:39 EDT 2006 | inds
Patrick, we were seeing a good amount of Cu-dissolution with both SAC305 and SN100C.. couldn't figure out.. till our good old vendors told us that the Cu thickness in the barrel were not correct... but anyway have started some new work with SAC30
Electronics Forum | Thu Mar 29 07:37:45 EDT 2012 | davef
The current discussion about solder fountains has to do with copper dissolution. Broadly, copper dissolution is the weakening of copper traces where a trace and a barrel plating intersect due a loss of the copper into the solder. Longer contact time