Electronics Forum | Mon Oct 16 00:45:33 EDT 2000 | soza
Dear sir, I have a problem to find the new chemical solution instead IPA(isopropyl alcohol) to eliminate contamination on the test pin socket board made from copper that plate with nickle and gold. And after the often testing IC process, the co
Electronics Forum | Fri Apr 13 21:02:19 EDT 2007 | Sam
Anyone experience using SnPb wire to gold plated ICs? I have tried to solder the SnPb wire to the gold plated ICs lead, but the surface finishing is dull. Can anyone explain that to me? Why it is not shinny surface? Any recommendation?
Electronics Forum | Fri Apr 25 14:49:34 EDT 2014 | isd_jwendell
If the tab is Sn plated, you can solder to it as long as your iron has enough power (watts). If you continue to have trouble then it probably isn't Sn plated.
Electronics Forum | Tue Apr 22 12:33:35 EDT 2014 | barryg
No we have a battery spring that is soldered directly to a PCB (standard tin plated copper PCB). The Battery spring supplier (and I have no confirmation he makes them or buys them) claims they are tin plated. When trying to solder to them it is very
Electronics Forum | Mon Apr 16 09:12:23 EDT 2007 | davef
Standard for appearance: J-STD-001 and IPC-A-610 committees eliminated the requirement that solder connections be "bright and shiny". Certain solderability protections; such as Au, NiPd, NiPdAu; can affect the surface texture of a solder connection,
Electronics Forum | Sun Apr 15 23:35:14 EDT 2007 | Sam
few more questions: Is there any standard saying that the dull surface is accepted if solder Au plated leads? Understand that more than 3% Au in the solder connection leads to unacceptable embrittlement of the connection. How about any standard relat
Electronics Forum | Mon Apr 21 16:38:45 EDT 2014 | barryg
Hello all. We have been having some problems soldering to what we believe is a nickel plated spring steel battery terminal to a PCB. We have tried scrapping , then tinning, dipping and still have problems. Are there any special fluxes or pre-treats t
Electronics Forum | Sat Apr 14 09:28:58 EDT 2007 | davef
When soldering a component to a board, the solderability protection on the component combines with the solderability protection on the board and the solder to form an alloy. This alloy is unique for that combination of solder and solderability protec
Electronics Forum | Thu Feb 19 16:02:49 EST 1998 | Gary Simbulan
I have been involved in SMT for only a few months so I am coming from a position of extreame ignorance. I have been asked to investigate the differences in soldering to components with Paladium coated leads vs the standard Tin_lead. I would appreci
Electronics Forum | Thu Oct 30 21:55:13 EDT 2014 | davef
Why soldering issues? I'd guess the nickel is corroded. It is very difficult to solder to oxidized nickel. Your SAC305 would get kicked all the way down the conveyor by nickel oxide. A lack of Ni-Sn-IMC formation will confirm this dewetting . What's