Electronics Forum | Tue Aug 08 20:42:11 EDT 2006 | John Erickson
Hello all, just wanted to say that I've been using MS2 for 2 months now. Yes, it does eliminate dross. Yes, it is a little messy. However, we've seen a significant drop in our DPMO's on both leaded and lead free process. The solder is so much cleaner
Electronics Forum | Thu Aug 05 06:29:18 EDT 1999 | Graham Naisbitt
| | | We're getting field failures in a high impedance portion of the circuit. Think the unpopulated pc card has contaminates because we were able to grow dendrites by applying a 9 volt battery across the suspected pad, placed a drop of de-ionized w
Electronics Forum | Sat Feb 05 21:58:08 EST 2000 | Stu Leech
I agree with all of the previous comments. 1) Here are a few things to keep in mind when cleaning with water. To effectively clean, any liquid must wet the surface. By itself, water has a surface tension of 70 dynes/square cm. This is relaively hig
Electronics Forum | Mon Mar 29 09:33:37 EST 1999 | Chrys Shea
| I require some feed back from any one who knows about using a voc free flux in a nitrogen wave solder machine soldering both through hle and smt componants. | What disadvantages are there when using this flux? | Do you have any contact details with
Electronics Forum | Tue Mar 30 08:11:27 EST 1999 | George Steele
| | I require some feed back from any one who knows about using a voc free flux in a nitrogen wave solder machine soldering both through hle and smt componants. | | What disadvantages are there when using this flux? | | Do you have any contact detail
Electronics Forum | Thu May 23 22:17:47 EDT 2002 | davef
Not intending to undercut Mike's offer, but to compliment it. Consider asking Heraeus for guidance about cleaning the residues from reflowing your paste. Some NC flux res: * Cannot be cleaned. * Can be cleaned after a relatively short period of tim
Electronics Forum | Tue Nov 29 12:53:56 EST 2005 | bschreiber
Hello Billy, You are correct when you say that you may want to look at the detergent (chemistry) you're adding to the stencil wash. However, "geared for epoxy removal" depends on how the chemistry is designed to remove the epoxy. If it is a "water
Electronics Forum | Wed Mar 15 17:37:30 EST 2006 | Dan Feinberg
Greetings all, Dross has no value to the assembler. It actually degrades quality as a clean solder pot provides a more consistent process. Yes, removing dross does remove some metallic contaminates but that is overkill, like throwing away your refrig
Electronics Forum | Thu Mar 16 10:55:23 EST 2006 | Baer
I can tell you that I have been involved in new process chemical introductions for 40 years. I have seen a lot of claimes and this is one of the best inovations I have seen. If I was not convinced of this I would not be involved. As for process impr