Electronics Forum | Mon Dec 14 10:53:10 EST 1998 | Earl Moon
| Has anyone had any experience with using this alternative plating process? Some board houses are pushing toward this plating. Is there any long term data on this process? Any problems experienced with smt and thru-hole? I've heard tin whiskers to b
Electronics Forum | Wed Feb 23 00:45:49 EST 2011 | tsvetan
Does someone with technical knowledge knows what exactly happend with the solder paste after the shelf life pass? What we have seen is sometimes flux separation which disapear after a good mix, and change of viscosity i.e. drying. The tin, silver and
Electronics Forum | Tue Aug 31 17:36:36 EDT 2004 | davef
NO-LEAD COMPONENTS WITH LEAD SOLDER ISSUE: We agree with Russ. We've dicussed this several times on SMTnet. For instance, look here http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=25394 LEAD COMPONENTS WITH NO-LEAD SOLDER ISSUE: We disa
Electronics Forum | Fri Nov 07 15:57:56 EST 2003 | Marc Simmel
Are there specifications or recommendations for electro-deposited tin-lead plating thickness on austenitic stainless steel that would provide a shelf life of 1 year? 6 months? Would 2 to 3 microns (78 to 118 micro-inches) 90/10 tin-lead over 1.27 mi
Electronics Forum | Sat Nov 08 10:04:26 EST 2003 | severs
Once you have selected your plating based on electrical and physical requirments, you should know that there is an inexpensive plastic storage packaging developed by Lucent which can keep any platings solderability from degrading for up to 10 years o
Electronics Forum | Fri Mar 18 14:22:37 EDT 2011 | bradbriggs
We recently ran into a situation where a SMT header with tin plated tails would not wet properly during reflow. Someone told us that tin plating has a shelf life and needs to be re-tinned after a length of time. I have not heard of that before. Do
Electronics Forum | Thu Feb 22 04:00:02 EST 2001 | Scott B
We are increasingly being asked to store components for longer and longer periods which we know through experience leads to reduction or total loss of solderability of the parts. 1) What is the industry accepted shelf life of tin/lead plated compone
Electronics Forum | Fri Mar 18 15:39:18 EDT 2011 | bk
Tyco had a good read on the shelf life of tin plating and the different variables involved in determining it's shelf life. http://www.tycoelectronics.com/documentation/whitepapers/pdf/Keeping_Tin_Solderable.pdf
Electronics Forum | Wed Jul 07 11:49:34 EDT 2004 | Svensen
Curiously... Shelf-life of the plating alternatives has been mentioned several times as a potential issue in these discussions. Tell me is there a market for a simple plastic packaging which could extend shelf life (and hence solderability) of these
Electronics Forum | Thu Aug 29 07:21:28 EDT 2002 | nifhail
What are other testing/process step that we should do if we where to use the old date code QFPs other than solderability and baking ? What is the plating composition normally %? lead, % tin etc. I have my policy not to accept the more than 12 mont