Electronics Forum | Mon May 31 15:09:56 EDT 1999 | JohnW
| | | | | | | | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processi
Electronics Forum | Mon May 31 15:10:14 EDT 1999 | JohnW
| | | | | | | | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processi
Electronics Forum | Mon May 31 21:50:59 EDT 1999 | Dave F
| | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processing a double-
Electronics Forum | Tue Apr 27 12:19:17 EDT 1999 | John
Has anybody had experience wavesoldering 1 watt 2512 resistor packages?? I know it can be done, but are there reliability issues? We are in the middle of a new product and the question was posed to me "Can we use 2512 1 watt resistors on the bottom
Electronics Forum | Sat Sep 26 22:08:07 EDT 1998 | Jeff Sanchez
I recieved a pack of sensitive IC's that said they needed to be baked befor certain processes. If I need to do rework, do I have to bake prior to single soldering of these IC's. Or can I just place one as needed by hand with out baking? Any info woul
Electronics Forum | Mon Sep 28 08:35:15 EDT 1998 | Earl Moon
| I recieved a pack of sensitive IC's that said they needed to be baked befor certain processes. If I need to do rework, do I have to bake prior to single soldering of these IC's. Or can I just place one as needed by hand with out baking? Any info
Electronics Forum | Fri Dec 17 08:29:18 EST 1999 | Wolfgang Busko
Hi Chuck, let�s say it the other way round. We use noclean since I can�t even remember without nitrogen and all of our subcons do with no known problems. The processes are adapted to it and no complaints are heard up to now. That is related to our pr
Electronics Forum | Thu Dec 16 11:54:45 EST 1999 | Mike Naddra
At reflow an inert atmosphere is used to mitigate the occurance of oxidation, to me the decision weather to move from an inert atmosphere is based on several things ; PCB surface finish - are you using a HASL finish, OSP or another surface finish and
Electronics Forum | Thu Dec 16 17:50:03 EST 1999 | LUIS LOPEZ
Hi, I am new on this, I want to ask you what is HASL finish, OSP, FPY, ppm. About to eliminate the Nitrogen in reflow soldering, a listen about one solder paste that no requires Nitrogen, the solder paste is called Indium, I don't know if this is tru
Electronics Forum | Tue Dec 21 08:33:54 EST 1999 | Nancy V
Luis, Go to the library on SMTnet and you will see Standard and Terms. Select that and you will be able to download the terms and definitions for SMT assembly. It is very useful. Of the terms you requested, only FPY is not there. I was curious a