Electronics Forum | Wed Aug 08 12:14:26 EDT 2012 | jorge_quijano
Hi, We have a client requiring us to use a Vapor Phase Reflow Oven instead of our convection oven, the new PCB design will be ~9.3mm thick with some SMD & Pressfit connectors, does the PCB thick could be the cause of they requiring us the Vapor Phase
Electronics Forum | Fri May 07 23:43:10 EDT 2010 | jlawson
I assume you using a fixed mass vapour phase system? Yes rates of rise are impacted by the mass of the PCB, larger the mass to mass of vapour phase the lower the rise generally. So if you load the machine with very little mass PCB rise times can be
Electronics Forum | Sat Jun 14 09:01:03 EDT 2008 | woo10
Is anyone out there using vapor phase soldering techniques? 1. I'm wondering what results you are getting? 2. How are you controlling the thermal profiles (specifically ramp rates and TAL)? 3. What fluid type are you using? Who is the mfg? Thanks
Electronics Forum | Tue Oct 12 11:54:23 EDT 1999 | Brian
| We (Compunetix, Inc.) need to sell a Centech Vapor Phase. What would be a good asking price. | | TIA | You should be aware that vapour phase is on its way down the hill for environmental reasons. In any case, how can anyone recommend a price wit
Electronics Forum | Wed Sep 05 13:45:36 EDT 2007 | john_smith
Ian, We currently have 2 inline vapor phase ovens and 1 batch oven. Tomb stoning is inherant with the Vapor phase systems but most can be stopped with a good profile. Most of our mechanical problems occur with the inline ovens during carrier transfer
Electronics Forum | Wed Mar 19 20:40:27 EST 2003 | arminski
Vapor Phase process can do reflow from 4 to 5 times!
Electronics Forum | Fri Aug 26 11:22:07 EDT 2005 | GS
Have you considered to use Vapor Phase Reflow(Condensation) ? Regards GS
Electronics Forum | Sat Apr 18 05:09:08 EDT 2009 | alfred
I have a solution.... contact me by mail Vapor phase gives a solution to that problem
Electronics Forum | Tue May 03 12:26:43 EDT 2011 | cyber_wolf
Your solder paste supplier can give you a recommended profile.
Electronics Forum | Thu Jun 12 10:26:27 EDT 2014 | jax
For Vapor Phase: approximately .04 bar or 30 torr for around 10 seconds.