Electronics Forum | Tue Mar 15 17:58:56 EST 2005 | darby
Mat, Are you sure you should be using SnPb HASL boards if you are doing prep for lead free? If you aren't actually going to comply with RoHS then fire away. Nearly all of our assemblies are now ENIG and as any re-design comes up on a HASL board it is
Electronics Forum | Wed Nov 23 17:24:43 EST 2005 | adlsmt
With Jars you tend to mix used paste back in with new paste and there is also a lot of air in the jar. If you are high mix try using cartridges and putting the used paste in little ziplock baggies. You can rip the baggies open including tearing the s
Electronics Forum | Mon Mar 05 07:59:11 EST 2007 | jdengler
Mark, I will begin by saying I am a big fan of Fuji equipment so I would not recommend anything else if you already know them. You say you get 70K placements a month with these 2 lines? Do you mean 70K boards a month? The first place to look a
Electronics Forum | Tue Mar 06 13:14:55 EST 2007 | stepheniii
I personaly have used both and for where I am currently Mydata is best for us. However I agree with the stick with what you know suggestion. Go Fuji. Make sure your management isn't looking at Mydata for fast changeovers. Process is the main facto
Electronics Forum | Thu Aug 06 11:02:18 EDT 1998 | Jim Price
| | Dew: | | Is this the third or forth software alignment for Fuji? Hope they stick with Unicam for a period of time... | | Just my two cents.... | I believe it's the forth, MCS OS/9, MCXE,F4G, and now fujicam...were there any others I missed? | Pe
Electronics Forum | Mon Aug 31 10:28:11 EDT 1998 | Patrick O'Connor
| | | | Dew: | | | Is this the third or forth software alignment for Fuji? Hope they stick with Unicam for a period of time... | | | Just my two cents.... | | I believe it's the forth, MCS OS/9, MCXE,F4G, and now fujicam...were there any others I m
Electronics Forum | Tue Mar 15 07:59:07 EST 2005 | mattkehoe
We are looking for some feedback on this situation. Please let us know if you have any ideas. Thanks in advance. I have been doing some studies on defects and such with our PCB's in prep for lead free and I've come to a conclusion about our process.
Electronics Forum | Tue Mar 15 09:46:06 EST 2005 | davef
Comments are: * J-STD-001 and A-610 committees have eliminated the requirement that solder joints be "bright and shiny". Certain metallizations (such as gold) can influence the solder joint surface texture, but have no impact of reliability. Reliance
Electronics Forum | Fri Mar 02 16:56:37 EST 2007 | vickt
Mark, How about a "line booster" such as the Universal AdVantis AC30L? The Lightning head provides a huge boost in throughput for your existing line, while also adding to the component range. One solution is to put it in the middle of a line to retur
Electronics Forum | Tue Mar 06 14:56:07 EST 2007 | rob_thomas
This is an interesting task you are faced with. If I understand you problem you need to double your throughput ? Is that correct ? If that is the case there are so many more factors to consider besides your equipment, adding more shifts etc. First o