Electronics Forum | Tue Mar 22 08:05:59 EST 2005 | jdumont
Morning all, my question is regarding the use of filled/tented/plugged vias on the BGA site. What are you guys doing for this? What type of issues can this cause if using none, or the improper via design. Regards, JD
Electronics Forum | Tue Aug 23 03:42:10 EDT 2005 | Adeline
presently, the production facing this problem. We has couple of brd which is electroylic gold finishing with plug via. The brd has blister after the PCBA (in lead free temperature, 265 degree) Some time, bare brd already has the blisters. But most of
Electronics Forum | Fri Dec 01 13:30:08 EST 2017 | kojotssss
Stencil thickness is 4 mil. Via's are plugging from bottom. Gas may be developed under the component? Take Reflow Ovens Thermal Profiling changes? In your opinion?
Electronics Forum | Thu Dec 07 00:55:51 EST 2006 | billylim
As you are aware the common method to rework BGA is : 1. Remove BGA with hot air reflow machine ( SRT as current practice) 2. Clean the BGA pad using solder iron and solder wick. 3. Replace BGA with SRT rework machine. The problem we have with
Electronics Forum | Mon Mar 07 10:14:31 EST 2005 | jmedernach
Cellular and PDA architectures employ this technology all the time. You have to be careful with your board supplier as well as with your plugging approach. Leave the via unplugged, I guarantee voids in the solder joint. That leaves us with, "how d
Electronics Forum | Thu Mar 03 08:06:36 EST 2011 | scottp
I've seen this with through hole via in pad with soldermask plugging from the opposite side. Baking the boards solved it. Not using such a horrible via in pad method would also have solved it, but that wasn't an option. Is this ball sitting on a v
Electronics Forum | Fri Aug 22 09:44:45 EDT 2003 | davef
Kenny: Since you need to use water soluable flux and can't use no-clean, consider asking your board fabricator to plug the via.
Electronics Forum | Fri Jun 09 17:34:08 EDT 2000 | Melanie Mulcahy
I need some information regarding the acceptability/unacceptability of using tented vias with LPI soldermask. Long story on all involved, but basically I have a board that I have had manufactured with no problems which has BGA/uBGA parts, tented via
Electronics Forum | Wed Sep 22 22:32:40 EDT 1999 | Dave F
| We are finding solder shorts under 1206 Components on the bottom side of our boards.In all cases these shorts are from either side of the component to a feed-thru under the component body. Adhesive is used to glue down the component and then the bo
Electronics Forum | Tue Jul 27 16:44:31 EDT 1999 | Earl Moon
| | | Presently protos of micro-bgas (80i/o) pitch .030/.031 | | | 12BGA per assembly | | | | | | The board is a (.062, 4 layers) FR-4 using Dry film | | | Pads .014inch | | | Vias within footprint .020inch | | | Vias to be filled by bottom side(sol