Electronics Forum | Tue Apr 29 07:12:49 EDT 2003 | Glen barden
Sn/Cu/Ni is introducted to me in wavesoldering lead free process. Around in our industry, we have a plenty of info. about SAC but not on this alloy. The distributor showed me some information about this alloy including less dross, more shiny /smoot
Electronics Forum | Mon Jul 20 17:40:48 EDT 1998 | socheat khun
| Does anyone know why this typically occurs. We have seen capacitors crack due to stressing. Any good solutions? | Regards, | | Steve. Hi steve! Did you check component date-code, reflow profile and component placement height. it has happen to me
Electronics Forum | Mon Sep 14 04:36:53 EDT 1998 | Frank Ferdinandi
I am trying to find out if it is possible to wavesolder TSOP's. If so , what should the footprint be like, and how should the wavesolder process be set up ? Alternatively can PLCC's be wavesoldered ? I would greatly appreciate any help. Regards Fran
Electronics Forum | Mon Oct 18 05:31:38 EDT 1999 | Mattias
Does anyone have any experience of popcorning BGA�s in wavesoldering?
Electronics Forum | Sat Oct 21 07:50:15 EDT 2000 | Adam
A question for all you wavesoldering buffs out there ? What i'd like to know is what causes the bulb-shape type joints around chip components when flowed over the wave ? which wavesoldering process parameter contributes to this type of defect & how
Electronics Forum | Wed Sep 27 09:36:46 EDT 2000 | Daniel Carlsson
Does anyone have knowledge concerning popcorning in wave-soldering. Is there a problem with moisture when the reflowed bords are left in air environment for days when manually assembled and then wave-soldered. Is there a certain temperature at which
Electronics Forum | Fri Feb 25 05:42:17 EST 2000 | Istv�n Dominik
Hi, We should wavesolder a PLCC44 package. The PCB is under the design procedure now and we must specify the best parameters (the orientation (45 or 90 degrees) of the package on the PCB,the number, the positon and the size of the solder thief pads
Electronics Forum | Fri Feb 25 05:42:17 EST 2000 | Istv�n Dominik
Hi, We should wavesolder a PLCC44 package. The PCB is under the design procedure now and we must specify the best parameters (the orientation (45 or 90 degrees) of the package on the PCB,the number, the positon and the size of the solder thief pads
Electronics Forum | Fri Jan 19 06:49:34 EST 2001 | Adam
To you wavesoldering guru's. When wavesoldering with a selective wavesoldering carrier What causes the white vapor type residues around the areas of the carrier which are exposed to the wave ? My Initial reaction was to high of A Pressure for the spr
Electronics Forum | Thu Jul 05 11:26:22 EDT 2007 | cokedigits
i defagree