Electronics Forum | Tue Apr 14 09:38:07 EDT 1998 | Earl Moon
| We are having some difficulty soldering a 240 pin Altera device. We use Alpha WS-609, a very generic profile for that solder paste, and a 6 mil stencil with laser cut apertures (1:1 ratio). This is a 20 mil pitch device (aperture size is 10 mils X
Electronics Forum | Tue Apr 14 09:01:36 EDT 1998 | Justin Medernach
| We are having some difficulty soldering a 240 pin Altera device. We use Alpha WS-609, a very generic profile for that solder paste, and a 6 mil stencil with laser cut apertures (1:1 ratio). This is a 20 mil pitch device (aperture size is 10 mils X
Electronics Forum | Sun Mar 15 23:58:01 EST 1998 | Phill Hunter
| | I am having a problem with Entek coated boards. The solder past seem to just ball up on the pads. I had no problems with the board when it was hot air leveled. The board is double sided surface mount. I have tried adjusting the oven profiles m
Electronics Forum | Thu Jan 08 15:03:40 EST 2004 | dwzeek
We have an ongoing problem with our QFP144 packages soldering. It has not received much attention until late due to some customer failures. Most of the failures would show up in ESS testing and be repaired. The failure rate is about 2 in 1000 parts f
Electronics Forum | Mon Jan 21 19:22:38 EST 2008 | davef
In your situation, the issue is the compatibility of your flux residues and the encapsulant that you choose. First, contact your encapsulant supplier for advice. They've likely been down this road with other customers and may be able so save you som
Electronics Forum | Thu Jan 08 16:16:09 EST 2004 | Dean
My first concern would be the choice of solder paste you have. There are better chemistries out there that far exceed the capabilities of the 609 2. Yes, the part will partially float on the solder (assuming plastic qfp). Cross sectioning would sho
Electronics Forum | Mon May 31 21:50:59 EDT 1999 | Dave F
| | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processing a double-
Electronics Forum | Sat Mar 08 11:04:47 EST 2003 | Joe
Mark, You've already received some good advice from the other posters. The one thing I would add is that even if you solve your printing issues on this type of part, the relative small quantity of paste may be prone to soldering problems. Ever s
Electronics Forum | Sat Apr 19 10:45:43 EDT 2003 | Joe
Yngwie, In a previous life, I used a mixer made by Malcolm and was very happy with it. We used Alpha 609 WS paste and experienced no separation problems. The Malcolm equipment agitated the material in a non-concentric motion which tends to "fold
Electronics Forum | Sat May 29 16:56:26 EDT 1999 | Jeff Sanchez
| | I have always thought it to be a good practice to wash SMA's with water soluble paste (WS609) soon after reflow. Is there a time limit as to how long a board should sit after reflow before washing said board? For instance; processing a double-