Electronics Forum | Mon Apr 26 14:40:07 EDT 2010 | blnorman
We had one product that used immersion silver plating. There were a couple of instances where we saw tarnishing, and elemental analysis confirmed the presence of sulfur. These boards did have the anti-tarnish sheets between boards, but somehow they
Electronics Forum | Thu Apr 29 18:48:11 EDT 1999 | Kiet Dang
Hi, Did anyone experience a problem with electrically conductive silver filled epoxy is resistive due to galvanic reaction? I'm having this problem when attaching components to Ni plated housing while conducting an experiment to cost reduction for Au
Electronics Forum | Thu Mar 25 02:22:32 EST 1999 | P.L. Sorenson - Technical Consultant
| | | Your problem may be related to silver migration (leaching) into the solder. I had what seems to be a similar problem. The solution was using solder with 2% silver content. See these pages for a bit more information: | | | | http://www.ferr
Electronics Forum | Thu Aug 21 22:47:39 EDT 2003 | adlsmt
Well after reading all kinds of stuff about this I still question if it is my current problem BUT, how common is this??? I dont want to be afraid of the boogie man but it seems like a lot of folks are having problems with black pad. I have used imers
Electronics Forum | Mon Feb 20 08:25:13 EST 2006 | Rob
No problem. If you get no joy you're going to have to change the footprint to a 1206 or 1210. Murata have a range of high Q value inductors (50-60) & from memory Toko used to be pretty hot too. The terminations on the coilcraft part are listed a
Electronics Forum | Thu Aug 29 06:48:01 EDT 2002 | yngwie
I have seen several Imm Ag pad on the assembled board which have a copper colorleaching through the silver plating This happened on the pad which was not deposited with paste during the assembly process. Don't know if it is a problem, but we only
Electronics Forum | Mon Jun 26 23:33:20 EDT 2006 | KEN
We saw this condition over 3 years ago. It sometimes is called "champagne bubbles". The intemetalic formation is interrupted due to the micro voiding reducing mechanical strength. I discovered this on lead free test vehicles for a major computer
Electronics Forum | Wed Aug 12 22:18:42 EDT 2020 | stephendo
Almost all the people here buy boards with the metal already plated on. We are mostly assembly people. The ones you really want to talk to are PCB fab people. And if you want to look into plating PCBs, I would suggest you look up Black Pad. It hasn'
Electronics Forum | Fri Feb 23 10:24:24 EST 2001 | johnthor
We still build a legacy product with a primitive backplane using silver plated fork terminals for outside world connections. After some 20 years of no problems the fork terminals on raw stock PCBs were black and almost unsolderable. Because of the
Electronics Forum | Thu Oct 21 02:31:27 EDT 2010 | rok
OGER 4003C bounding to Aluminum I am hoping someone might have the solution to my problem I have the following PCB: RO4003 Thickness: .2mm Layer: top single/ bottom ground plane Finish: silver top and bottom .2um Size: 3mmx6mm I need to bound/groun