Electronics Forum | Tue Apr 05 09:10:12 EDT 2005 | Dave G
You may have to get him to see a dermatologist or allergy specialist. Also, analyze exactly what he's coming in contact with during the course of a workday. Some people are allergic to what the rest of us have no trouble at all with. One thought - If
Electronics Forum | Thu Apr 21 00:09:12 EDT 2005 | Debbie Technical Devices
Any help locating a machine to remove foreign > materials from bare pcb's would be appreciated, There are several issues that should be addressed. There are several issues that should be addressed. Let's talk about your process and find out what
Electronics Forum | Sat Apr 09 13:42:03 EDT 2005 | jh0n!
how funny... we just bought a up1500, no manuals/install cd, and we need to do the same thing. i was hoping that by removing /sigpro/user.pwl and /sigpro/permis.lst, and all references to them in sigpro.ini and sig1500.ini it'd let me in, but no luc
Electronics Forum | Sat Apr 23 13:54:09 EDT 2005 | Indy
I don't know wat are the types.. but wat I can tell you is you need care while profiling them. it needs a peak of around 215-220 if Sn/Pb.. at the ball. So the plastic on top will reach a higher temp. Care must be taken so that it doesn't roast. al
Electronics Forum | Sun Apr 24 09:12:00 EDT 2005 | davef
We're not sure what your customer is talking about either. Gold and tin form an intermetallic compound [IMC] that can cause poor solder connections. To minimize the potential of a problem, keep gold to less than 3 percent of the metal. [Search the
Electronics Forum | Tue Apr 26 16:56:23 EDT 2005 | stepheniii
Is anyone using any NanoStar components from TI? It looks like we might be building boards with some soon. We have put down 0201's successfully. But these are a whole other ballgame. They are 0.9mm by 1.4mm with 5 or 6 balls on the bottom. Would thi
Electronics Forum | Thu May 05 09:17:58 EDT 2005 | jimmiem
I tried soldering to several of the black pads and was successful, the solder stuck with no hesitation. so i guess this is not truly "black pad"? would that be a correct statement? What causes this blackening that looks like oxidation under the mic
Electronics Forum | Mon May 09 18:43:58 EDT 2005 | keegomaster
Hi everyone! Me and my R&D team are working on the design of a highly flexible AOI. I'd like to know your "wishlist" on what you'd like a brand-new AOI to have. I gotta figure out the competitive advantage; what a better place than this "Agora". I'd
Electronics Forum | Mon Jun 06 09:05:02 EDT 2005 | cmiller
How do apply it in your process? It would seem best to screen the electrically conductive epoxy then dispense the thermally conductive epoxy to bond the part to the heat sink pad. Any help or opinions would be appreciated. I dont think the System Uni
Electronics Forum | Mon Jun 06 16:09:03 EDT 2005 | avalancher
Grant, As a MYDATA user, your comments worry me. You state that the MDYATA's are not stable or reliable? I am currently placing 0201's with the HYDRA head (at appx 15K/hr) with 0.01% fallout/bad placement. I also place a large range of fine p