Electronics Forum | Wed Feb 22 08:02:56 EST 2006 | dj44
I was looking for an stencil design for a 0.5mm pitch uBGA. Pad size is 0.38mm in diameter. We have been using 5mil stencil with type 3 no clean paste. What size aperture should we be using? Any suggestions?
Electronics Forum | Tue Aug 28 14:21:39 EDT 2001 | Scott B
You have to be careful here. The figure is expressed as placement accuracy, not process quality therefore 3 sigma does not relate to 2700 PPM defects but 2700 parts per million placed outwith 15microns (0.0006" / 0.6thou). Extrapolating the distribu
Electronics Forum | Mon Sep 24 12:58:31 EDT 2018 | vincentl
We are attaching 0.50mm diameter SAC 305 solder balls onto 0.38 diameter Au plated pins placed at a 0.80mm pitch (pins are pressed into a plastic insulator). A tacky flux is then stenciled onto the pins using a stencil with.a 0.38mm diameter aperture
Electronics Forum | Fri Aug 21 04:43:14 EDT 2009 | ghepo
Hello, I suggest you visit the website http://www.analysispcb.com, where I found these information : PARAMETERS FOR DOUBLE “V” SCORING LEAD FREE LAMINATES Typ WEB Thickness, 1.6mm : 0.38mm (+.15/-0) "...Tg is not a good indicator of a materials’
Electronics Forum | Tue Jun 05 21:14:10 EDT 2001 | davef
You aren't going to post our stuff on your "Hey, I'm the wizard site", are you? Board fab, Pad coatings, OSP 1 OSPs: Imidazole (Via Systems) is good. Entek (Enthone) works, but requires strict thickness control in fab. 2 Enthone CU56 allows one t
Electronics Forum | Tue Feb 04 22:28:16 EST 2003 | davef
You could reduce the paste by about 70%. Solder balling and tombstoning will be the issues to fight. The drivers to these don't change with the component size. Use the fine SMTnet Archives for background. Aperture Size and Thickness of Solder Pas
| 1 |