Electronics Forum | Thu Oct 05 16:12:09 EDT 2006 | Mario Scalzo, SMT CPE
* Try 1.5C / sec from RT to 165C * Hot soak at 165-175C for up to 2 minutes (I'd start with 60 seconds flat soak.) * 60-90 seconds TAL (I's start with 60) * 230-240C Peak. Thanks, Mario
Electronics Forum | Mon Nov 05 20:31:09 EST 2001 | davef
Most people do not intend to �solder� Type K thermocouples. They use solder to �attach� the thermocouple. Search the fine SMTnet Archives for a posting by Chrys Shea. 1 Common thermocouple types commonly used for thermal profiling are: * Type K �
Electronics Forum | Tue Feb 12 18:48:48 EST 2008 | larryd
Thanks for the spare change. Questions are good and I did miss one item. Process has 100% solder paste inspection with a 3D inspection machine that has very few false calls or accepts. Ramp to peak is less than 1.5C/sec. Profile looks good, solder
Electronics Forum | Fri Jan 24 16:54:24 EST 2014 | davef
Yeh, I worked at Wang Computer factory in a reclaimed fabric mill with wooden floors. One of the causes of grapping is flux loss. In their paper, Briggs and Laskey talk about flux loss due to spreading and suggest: * Graping is much less prevalent i
Electronics Forum | Sun Sep 28 17:14:53 EDT 2008 | ronsou
small pads like 0402 tend to get hot quite > easily. looks like excessive heat is your problem > here. pads are wetted, component leads are not. > this means solder paste flux on top layer was > exhausted before entering in reflow. your profile
Electronics Forum | Tue Sep 02 15:29:36 EDT 2008 | bvdl
small pads like 0402 tend to get hot quite easily. looks like excessive heat is your problem here. pads are wetted, component leads are not. this means solder paste flux on top layer was exhausted before entering in reflow. your profile is the 'in-be
Electronics Forum | Mon Apr 12 19:28:26 EDT 1999 | Tom B
Netters, When I reflow a PCB there is a discoloration of silkscreen and mask. It appears if Profile is too hot! But I dont think so, maybe I'm wrong? 1. Kester 293 no clean 2. 2.1 C/s for 30s to 150 C 3. .5 - .7 C/s for 60s to 185 C 4. 1.5 C/s u
Electronics Forum | Tue Apr 13 18:11:00 EDT 1999 | Jimmy Strain
| Netters, | | When I reflow a PCB there is a discoloration of silkscreen and mask. It appears if Profile is too hot! But I dont think so, maybe I'm wrong? | | 1. Kester 293 no clean | 2. 2.1 C/s for 30s to 150 C | 3. .5 - .7 C/s for 60s to 185
Electronics Forum | Mon Apr 19 11:21:03 EDT 1999 | Travson
| Netters, | | When I reflow a PCB there is a discoloration of silkscreen and mask. It appears if Profile is too hot! But I dont think so, maybe I'm wrong? | | 1. Kester 293 no clean | 2. 2.1 C/s for 30s to 150 C | 3. .5 - .7 C/s for 60s to 185
Electronics Forum | Mon Apr 19 20:49:13 EDT 1999 | Dave F
| Netters, | | When I reflow a PCB there is a discoloration of silkscreen and mask. It appears if Profile is too hot! But I dont think so, maybe I'm wrong? | | 1. Kester 293 no clean | 2. 2.1 C/s for 30s to 150 C | 3. .5 - .7 C/s for 60s to 185