Electronics Forum | Wed Jun 27 22:03:48 EDT 2012 | davef
Here's some notes I've collected over the years on the topic ... Small MRP * I havent used it [DBA Manufacturing] yet but I do find myself keep coming back to it - I have been searching for a decent ERP system for my micro company for years. What I
Electronics Forum | Thu Aug 05 18:21:16 EDT 2004 | davef
Well, it could be the beautiful Jill Masterson, as Goldfinger's trusted card advisor Shirley Eaton, who gave new meaning to the phrase "golden girl." Or more mundanely, gold thickness usually ends-up: * Gold fingers (10 to 100 micro-inches) * Selec
Electronics Forum | Thu May 02 09:33:30 EDT 2013 | 15009
Looking for advice on soldering lead free paste to a board with very heavy gold plating. I have learned from the Customer that this is HARD GOLD and that it is 10-20 Micro Inches Hard Gold over 100 Micro inches of Nickel. When we reflowed the solde
Electronics Forum | Tue Jul 23 11:06:00 EDT 2019 | majelacquinn
Currently trying to get away from using stencil printing. Looking for information on Micro-Dispensing and dot size using a Vermes MDV-3200A micro jet dispenser. I am using a Indium led free solder that has size 6 balls. With a 100 micron dispense hea
Electronics Forum | Thu Dec 29 22:19:36 EST 2005 | Joseph
We have tested SN100C for LF wave soldering process since August'05 and currently start production for a month ago. Initially we use SAC305, but due to the shrinkage cavities (micro-crack) we changeover to SN100C. In summary, SN100C did perform well
Electronics Forum | Mon May 14 18:31:20 EDT 2001 | genny
The experiment was to determine insertions from a > gold plated board into a connector. Same > thickness boards (0.062"), with 100 m base > nickel. � 100m gold =_ 500 insertions � 50 m > gold =_ 300 insertions � 30 m gold =_ 50 to 75 > insertio
Electronics Forum | Wed Nov 25 15:16:04 EST 2009 | sforman1
Why in heavens name are you using a heat or air cure conformal coating. Why aren't you using a 100% solids UV cure system. You would never have an issue like this Sam Forman MicroCoat Technologies
Electronics Forum | Mon Dec 29 08:54:46 EST 2003 | pjc
SPM is superior. SPM has larger print area, up to 20� x 19", vs. 17.7� x 15.7� for the UltraPrint 100. UP100 is microprocessor controlled while the SPM has a PC. The SPM cameras can be positioned more rapidly and with greater accuracy than UP100's.
Electronics Forum | Mon Apr 19 15:27:05 EDT 2004 | pjc
The MicroFlex is not really new. Its the UltraPrint 100 re-engineered and improved. UltraPrint 100 / SMTech 100 has been around for many years. I don't believe the DEK 248 offers a Stencil Wiper option. I worked on MicroFlex machines. Vision system i
Electronics Forum | Wed Jun 06 16:51:06 EDT 2001 | jax
Unless your placing micro-bga, board edge fiducials on alternating corners will provide more than enough placement correction ( Micro-bga's should also be fine depending on how your equipment maps the board ). The part data and vision recognition nee