Electronics Forum | Thu Oct 01 03:03:29 EDT 2009 | cunningham
what we are getting is open circuits not every BGA is failing we use Humiseal 1A33 and currently there is no masking instruction for around the BGA
Electronics Forum | Thu Oct 01 07:03:55 EDT 2009 | davef
We doubt that Humiseal 1A33 is causing opens in your assemblies. We'd guess the opens occur earlier in the process, but are not hard failures. So, you pass your tests. When applied, the conformal coat flows into the gap in the ball crack and insulate
Electronics Forum | Thu Oct 08 08:15:39 EDT 2009 | kpm135
We've used both 1A33 urethane and 1B31 acrylic coating on our SMT assemblies with great success for many many years. This is with components of all shapes and sizes including a 9 ball micro-BGA. We apply the coating in every way imaginable and we hav
Electronics Forum | Thu Oct 08 01:07:46 EDT 2009 | tpappano
I have used 1A33 for many years with excellent results on through-hole pcbs in equipment subjected to very hot and very cold environments. Because 1A33 continues to harden with time, I assumed it would simply not be usable on smt boards, cracking t
Electronics Forum | Tue Jul 03 01:54:42 EDT 2018 | rdhiman1
Reaching out to all conformal coating experts, please help! While setting up conformal coating using the automated atomized spray, we observing issues associated with conformal coating wetting on the following regions: 1) Component edges 2) Metalli