Electronics Forum | Mon Aug 20 09:49:57 EDT 2018 | dontfeedphils
Not entirely clear on your question. We don't coat any of our hardware (assemblies are coated prior to hardware installation), so if coating needs to be reworked after this, then hardware removal is needed.
Electronics Forum | Sat Aug 18 10:35:41 EDT 2018 | mgerrior
Hey Phil, i'm just curious what your rework processes are for your hardware after conformal coating is applied (if any). I'm interested in conformal coating as our hardware can be exposed to moisture rich environments at customer sites but to my kno
Electronics Forum | Tue Jul 03 01:54:42 EDT 2018 | rdhiman1
Reaching out to all conformal coating experts, please help! While setting up conformal coating using the automated atomized spray, we observing issues associated with conformal coating wetting on the following regions: 1) Component edges 2) Metalli
Electronics Forum | Tue Aug 14 16:18:48 EDT 2018 | dontfeedphils
A couple of things to try as I just went through this myself. Checkout this link for pointers on plasma cleaning... http://www.nordson.com/~/media/Files/Nordson/march/Papers/The-Effects-of-Plasma-Treatment-Prior-to-Conformal-Coating-NordsonMARCH.p
Electronics Forum | Mon Jan 28 11:50:23 EST 2013 | johng
Good morning Mark, No issues around the masking at this point. The issue seem to be in open areas as well as between clad runs. We are using Humiseal 1A33 Conformal Coat.
Electronics Forum | Thu Oct 01 07:03:55 EDT 2009 | davef
We doubt that Humiseal 1A33 is causing opens in your assemblies. We'd guess the opens occur earlier in the process, but are not hard failures. So, you pass your tests. When applied, the conformal coat flows into the gap in the ball crack and insulate
Electronics Forum | Mon Oct 03 21:02:23 EDT 2016 | rwd
I am doing some rework to my CCA. I then need to conformal coat the board. I'm using Humiseal 1A33 GEL and my jumper wires are teflon coated. I understand the chemical interaction between the 2 products. My question is "Is this an acceptable prac
Electronics Forum | Wed Mar 04 08:32:45 EST 2020 | stephendo
We bought a conformal coating removal machine AKA a sand blaster at an auction. It is a CCR2000 especially made to be ESD safe. Does anyone have any experience with sandblasting conformal coating? We mostly use humiseal 1A33 and UV40. When we use the
Electronics Forum | Mon Aug 29 16:21:20 EDT 2011 | rjlasko
Greetings...I have a customer that has an assembly that is conformal coated with Humiseal 1A33. This assembly has some components (resistors and FET's) that heated up during operation and has discolored the conformal coating around their location.
Electronics Forum | Mon Nov 25 03:14:57 EST 2013 | mg2013
Hello @ the specialists, we have a Nordson Asymtek SL940 to coat our pcb's. We can use the valves SC100 and SC400 for conformal coating applications. We use the Humiseal 1A33 as the conformal coating. Now we would like to use the standard 1A33 in th