Electronics Forum | Tue Nov 09 13:12:26 EST 1999 | Dave F
Steve: Sure, but let's figure it out for you!!! ;-) Here�s some sample calculations. Your results may vary, void where prohibited, etc 20 PITCH: Pinched aperture volume: 0.010"X0.050"X0.005" = 2.5 uin^3 Zippered aperture volume: (0.015"X~0.5)
Electronics Forum | Thu Aug 12 22:38:44 EDT 1999 | Dave F
| Hello | | Having a problem with bridging on 20mil pitch qfp, only on the lead groups where squeegee goes over width of apertures. Using MPM sp-200 semi-auto, chem-etch stencil, 9-10mil width opening | 100 durometer blade. Getting "tails" on deposi
Electronics Forum | Thu Jun 03 12:31:30 EDT 1999 | Dave F
| | | In a month or so, we will be getting an in-line x-ray inspection machine. It will require that we solder our most comlicated side (normally top) first. This is opposite to our process now where we solder our passive (bottom) side first. We
Electronics Forum | Thu Jun 03 14:40:22 EDT 1999 | JohnW
| | | | In a month or so, we will be getting an in-line x-ray inspection machine. It will require that we solder our most comlicated side (normally top) first. This is opposite to our process now where we solder our passive (bottom) side first. W
Electronics Forum | Thu Jun 03 14:41:06 EDT 1999 | JohnW
| | | | In a month or so, we will be getting an in-line x-ray inspection machine. It will require that we solder our most comlicated side (normally top) first. This is opposite to our process now where we solder our passive (bottom) side first. W