Electronics Forum | Wed Dec 20 13:40:11 EST 2000 | Roland
ECA- Electronic Component Assembly, Electronic Control Amplifier, Examination, Certification and Analysis (performed during IQT, Electronic Commerce Association,European Crystallographic Association, electronics contract assembly, Eastern Communicati
Electronics Forum | Wed Dec 20 21:32:47 EST 2000 | Dave F
You're correct it's a goofy question. Voltage is going to be circuit dependent, since the ball will be connected to the board. There's some ball dimensions in the fine SMTnet Archives ... they're about four times the diameter of your wires. If tha
Electronics Forum | Tue Dec 19 19:11:37 EST 2000 | Michael Parker
Not much activity here in the past few days. Just wondering if you all have been egg nogging it too much in preparation for jolly ol' St. Nick. Or could it be that some have taken to smoking the mistletoe? I hope DaveF. has recovered OK from his re
Electronics Forum | Wed Dec 20 21:12:20 EST 2000 | Dave F
There's a bunch of suppliers [Fabmaster, Unicam, GC-Place, CircuitCam] listed in the fine SMTnet Archives. You have to be a bit partial to CircuitCam, it's a ground-up product designed for our work by someone from the business, not some cobjob on a
Electronics Forum | Thu Dec 21 16:56:03 EST 2000 | lucky
I do not think so. The 54 mm has a large field of view, so when it looks at small parts the image is blurry. What you want to try is using the other camera (camera 2) it has a 38mm field of view. Camera 2 is considered a narrow field of view, the cam
Electronics Forum | Fri Dec 15 11:45:38 EST 2000 | DaveJ
All, Thanks for your quick response. However, my primary concern is not the question of solderability advantages of nitrogen versus air. With all things (zone temps, track speeds, flow rates, etc.) being equal, what would be the profile differences o
Electronics Forum | Thu Dec 21 20:13:02 EST 2000 | Brad Kendall
I used to switch my N2 on and off for different products and I had performed profiles on the products with and without the N2 on and there was not a difference in the profiles. So you should not have to adjust your profiles. I think everyone else c
Electronics Forum | Thu Dec 14 21:54:50 EST 2000 | Joseph Scott Dowsett
I am student at Northern Illinois University and am doing a senior design project on applying castellated solder pads (pads on the side of the substrate) to a hybrid circuit. I have had difficulty finding related articles. I found this website and
Electronics Forum | Thu Dec 14 19:38:28 EST 2000 | Dave F
OK, now let me ask the really dopey question ... so if the irregularity of the HASL surface is punching holes in the thermal gasket and causing shorts to the heat sink, why are you putting solder on that surface? I wonder how the thermal conductivit
Electronics Forum | Wed Dec 13 16:12:01 EST 2000 | C Dooley
Is it possible to find the Cpk value for attribute data? We are running into problems due to unspecified LSL/USL values. How can we find the Cpk values without specific LSL/USL? We would also like to get some reference books on this subject so any