Electronics Forum | Tue Jan 04 13:21:56 EST 2005 | BK
1. Yes, you are probably doing it now on a daily basis. 2. No, not if you want to meet the requirments for lead free.
Electronics Forum | Wed Jan 12 16:11:26 EST 2005 | russ
I have seen the solder shoot out at least 4"-6" from both the leading and trailing edge when this happens. If the open pockets are real deep you may want to use a turbulent/chip wave for soldering, sometimes this leaves bridges however.
Electronics Forum | Tue Jan 25 12:59:53 EST 2005 | Andrew Smith
Brad, You may want to give some of my customers a call in reference to the Assembleon machines. The newer style of P&P have windows NT which is much user friendly than the earlier generation. You can always drop a line back if your interested in
Electronics Forum | Wed Jan 19 18:24:09 EST 2005 | russ
Make sure that you are running the right leadfree profile. You may want to verify that it is correct with thermocouples. Use Indiums Tacflux023, This should work. As far as cleaning them after this I will have to leave up to you. Russ
Electronics Forum | Tue Feb 01 10:46:25 EST 2005 | Frank R.
I agree with you. And if you want a backup vendor in case of BO, I don't think it's possible to get it from an other company.
Electronics Forum | Tue Jan 25 09:53:18 EST 2005 | lyrtech
I wanna know if anyone has a maintenance schedule for an Electrovert Ultrapak 650C. If yes, can you give me some HINT to do that schedule? I'm new to that machine and I want to know all about it. Thanks a lot
Electronics Forum | Mon Jan 31 06:58:27 EST 2005 | Martina
Ciao, i want an opinion: in my factory any people says that it's possible, without problems, to test the vias with the probe! Any suggestion? Any problem if you know? Thanks! Sorry for my bad english, i'm italian! Bye!
Electronics Forum | Fri Jul 08 10:45:17 EDT 2005 | dougs
Jack, Your telling me to do what i wanted to do anyway, My first question on the thread was where do i get this type of software.
Electronics Forum | Mon Feb 07 12:47:18 EST 2005 | Indy
1. use 6-7mils stencil. 2. reduce aperture opening to 60-70% of pad size. 3. check viscosity of solder paste. According to that you might want to alter your print speed and pressure. Cheers Indy
Electronics Forum | Thu Feb 10 08:57:35 EST 2005 | etienne
I want to know how is your feel to buy components in 13" reels rather than in the 7" reels. Obviously enough is that machines will stop less for replenishment, but what about the value of the stock?? What is your comment?