Electronics Forum | Sat Jul 29 04:13:39 EDT 2006 | Olas
What kind of material is Durastone? The only I could find on Google is a stone used for tiles, but probably you are referring to another material. I hope it is not extracted from the same mines of Baohodium ;-) Regards, Olas
Electronics Forum | Sat Jul 29 04:20:12 EDT 2006 | Olas
Sorry, I found it. I typed Durastone instead of Durostone. Interesting material. Have a good day, Olas
Electronics Forum | Thu Jul 27 12:30:37 EDT 2006 | Rob
Hi David, we used the following techniques in high volume production, depending on the type of flexi-board: (all were in milled pockets in a durastone pallet) 1) Kapton tape top & bottom 2) Spray mount & samll amount of kapton tape (you only had
Electronics Forum | Thu Jul 27 12:49:39 EDT 2006 | SWAG
We use same methods of PCB attachment to carrier as Rob lists. To be more specific on pocket size, we machine our durostone carriers so there is 0.010 inch gap around perimeter of board. This might seem like a lot but (from my experience) you will
Electronics Forum | Thu Jul 27 12:20:33 EDT 2006 | David
Hello all, We have customer who wants to produce boards 0.4 mm thick. But they have not allowed to put into the panel. Board has not regular shape so without pallet it is not possible to produce. I made pallet where is pocket the same shape as boar
Electronics Forum | Wed Aug 23 02:48:11 EDT 2006 | ec
Hi, Appreciate someone could advise or forward a format to me how to work out number of pallet needed for wave-solder if the machine speed is at 1.0m/min, volume per month is 4500 sets, pallet length 0.3 meter, conveyor length 5 meter...... Looking
Electronics Forum | Wed Aug 23 08:08:25 EDT 2006 | aj
There are a few variables that you have to consider : 1. Hours available on Wave Machine ( are other products going thru the same wave) 2. What beat rate are the boards being supplied from previous station?i.e. do you envisage the waveto be a bottl
Electronics Forum | Wed Sep 13 08:23:59 EDT 2006 | davef
We get a more active flux.
Electronics Forum | Wed Sep 13 05:32:11 EDT 2006 | Rob
Hi Peter, are you talking about storage times after opening sealed packaging and the effects on solderability due to oxidisation/moisture sensitivity? Cheers, Rob
Electronics Forum | Tue Sep 12 01:50:22 EDT 2006 | meritajs
Hi All, We find out that some companents in leed free reflow soldering process have bad wetting and soldering This soldering problems caused by companent storage time after shipment Could somebody inform us about maximum storage time for different c