Electronics Forum | Fri Aug 20 15:13:37 EDT 2010 | dschlo
No the break aways do not contain metal.
Electronics Forum | Fri Aug 20 06:32:44 EDT 2010 | aj
Hi, I would recommend you trial an alternative supplier if you have the option. I did a lot of trials on the issue and dont have any problems. Contact me off line and I will share details aj...
Electronics Forum | Fri Aug 20 10:07:09 EDT 2010 | dan_ems
Hello, I have the same problem ..., please take a print screen with the profile to see how is made it. Thank !
Electronics Forum | Fri Aug 20 10:49:37 EDT 2010 | cobar
Article to assist with Stencil Design Guidelines http://shanelo.co.za/technical_paper_about_stencil.htm
Electronics Forum | Fri Aug 20 01:52:49 EDT 2010 | arek
Please send me everything what you have to a.nowicki@propox.com Thank you
Electronics Forum | Fri Aug 20 10:11:19 EDT 2010 | namruht
I just found out that we have an older Omron VT-WIN that we are not using. I do not know anything about the machine, but I am curious if it is worth trying to bring onto the production floor and use it for inspection. Can anyone tell me anything abou
Electronics Forum | Fri Aug 20 10:47:05 EDT 2010 | dschlo
I am looking for a company that recycles the scrap created when boards are depanelized. Specifically for CEM3 Material.
Electronics Forum | Fri Aug 20 15:01:19 EDT 2010 | davef
Companies accept boards for recycling based on their expectation of making money by recovering the metal from the boards. Do your side rails contain metal?
Electronics Forum | Fri Aug 20 15:23:43 EDT 2010 | davef
It'll be interesting to see if they take them. Look here for board recycling houses: http://www.smtnet.com/Forums/Index.cfm?CFApp=1&Message_ID=55677
Electronics Forum | Fri Aug 20 09:40:56 EDT 2010 | namruht
kpm, We were afraid of that, so we have tried several variations with paste usage. New paste, transfered paste from another line, and a new tube from another date code. I think the problem is profile, board design or humidity. I just have to starti