Electronics Forum | Tue Jun 15 08:22:39 EDT 2004 | jsmith01
The parts are dated Mar 20 2004. My profile hits a peek of around 232-240c and is above 225 for around 30 seconds.
Electronics Forum | Fri Feb 27 16:02:20 EST 2004 | Zaxx
Hi Paul, One way but it slows down the process, is to get fixturing pallets made. You can usually get a universal fixture made for anywhere from $185-225USD. Hopefully this can help. Sincerely, Zack Schmad
Electronics Forum | Mon Jun 14 17:21:31 EDT 2004 | russ
How old are these parts? Sn/Ni plating is very succeptable to age and everything else. They are possibly tarnished. Also, what is your peak temp in reflow? It takes about 225 230 C to get good wetting to the underlying nickel. Russ
Electronics Forum | Mon Aug 23 12:13:57 EDT 2004 | ozzy
I have problem finding the values of two caps that are surface mount. There ID's are: One cap has a code of 1A5 the other cap has 225 16g 408 (yellow with a stripe) Thanks
Electronics Forum | Wed Dec 15 08:44:50 EST 2004 | cardinal
Hi Patrick, For UP 78 the best profile is also the easiest. Straight ramp to 220-225 1-2 degrees C per second TAL 45-60 seconds drop it staight off The Tech bulletin says the exact same thing. Former Alpha Guy here
Electronics Forum | Mon Jul 19 21:25:28 EDT 2004 | davef
It seems like the flux is burning-up before the metal begins to flow on this slightly odd component. Alpha talks about alternate reflow recipes for WS609, as follows: * A straight ramp up profile is preferred for reflowing low to medium thermal mass
Electronics Forum | Fri Apr 23 13:31:20 EDT 2004 | russ
The toes of leaded devices are problematic in fillet formation. A lot of the time they have the copper from the lead exposed so it becomes oxidized and won't readily take solder. Normally this is of no concern if the heel and side fillets are forme
Electronics Forum | Thu Jan 08 16:43:43 EST 2004 | Dean
Unless your machine (internal) thermocouples are each calibrated and compensated no two machines will deliver eactly the same results. Here are your challenges: 1. Data acquisition equipment A-D converter errors 2. PCB measurement thermocouple (t
Electronics Forum | Wed Apr 21 18:24:13 EDT 2004 | pjohnson@volterra.com
Simple process - we use similar Kester solder brands of "no clean" low residue solder wick to clean our pads, then brush with isopropyl, and apply Kesters brand of tacky flux under a Leica 6x microscope. We do this on 7x7mm and 9x9mm packages. This w