Electronics Forum | Thu Jun 01 04:51:21 EDT 2006 | EC
Hi TS, Most of the machines will face this problem after been using few years.....I handling SMT equipments ( Fuji machine ) and process.....sorry if I have offened you...... Hi Jack, Firstly, you must able to tell which component having a high thr
Electronics Forum | Fri Jun 23 10:10:15 EDT 2006 | Gman
Some amount of voiding was always seen on sites where solder paste is printed. These voids are much smaller. However the site where a flip chip is flux dipped has never had problems with voiding. Macro voids (and huge ones at that)across the board s
Electronics Forum | Mon Jun 26 23:33:20 EDT 2006 | KEN
We saw this condition over 3 years ago. It sometimes is called "champagne bubbles". The intemetalic formation is interrupted due to the micro voiding reducing mechanical strength. I discovered this on lead free test vehicles for a major computer
Electronics Forum | Mon Jun 26 12:23:11 EDT 2006 | Rob
Yep, Book a holiday and let someone else sort it out. Otherwise e-mail me and I'll talk you through pallets, rigidisers, printer tooling, spray mount, Kapton tape, local fiducials (panels can strech & shrink) etc. Oh, yeah - for the connectors you
Electronics Forum | Fri Aug 18 11:01:52 EDT 2006 | Frank R.
Hi, We have two complete SMT line and in this department we use conveyors for board manipulation. Concerning the wave area we are not full efficiency and I have to look for conveyors and bar code reader to make board manipulation an automatic proces
Electronics Forum | Tue Aug 22 20:32:40 EDT 2006 | davef
Fixed position (mounted) [In-line] laser bar code scanners: * microscan 800.762.1149 info@microscan.com [Ken SMTnet] * symbol technologies symbol.com [Russ SMTnet] * Keyence and RVSI inline scanners [B Norman SMTnet] * Datalogic TC1100 bartec-systems
Electronics Forum | Thu Aug 24 16:08:18 EDT 2006 | Frank R.
Thanks Bill and Dave for your help, Sorry Dave if I didn't search for information in archives. After wave process we have 2 ICT, 2 AOI machines 4 PVA conformal coating machine that will be use on 3 different lines. The quind of automation I want to
Electronics Forum | Tue Dec 19 16:26:24 EST 2006 | samir
Grant, Newer lead-free fluxes have 6%-10% solids content - more activator, therefore leave more "visible" residues. Old technology tin-lead fluxes got down to as low as around the 4%-6% range (I'm going off memory, so me might be wrong)... You'll
Electronics Forum | Wed Dec 20 04:43:36 EST 2006 | greg york
Any decent flux would volatise off with the heat of the wave unless absorbed into the solder mask. Test this by trying to clean in alcohol or common solvent aerosol, if it does not clean then it is probably Mineral Salts from solder mask fillers. Ano
Electronics Forum | Sat Jan 29 08:46:20 EST 2005 | davef
The RoHS Directive complements the WEEE Directive. * Restriction of Hazardous Substances in Electrical and Electronic Equipment (RoHS) Directive [2002/95/EC] affects manufacturers, sellers, distributors and recyclers of electrical and electronic equ