Electronics Forum | Sat Jan 17 17:42:07 EST 2009 | viresh
what is the impact if a solder paste is used after 24 hours after tawing time
Electronics Forum | Mon Jul 12 20:26:10 EDT 2021 | stephendo
A test that I would like to see is, expose parts for 24 hours 40%-60% RH, 25C for 24 hours. Then seal with a HIC and minimum desiccant that Jstd 33 requires. Five to seven days later open and see if HIC says good but parts have excess moisture. I t
Electronics Forum | Thu Oct 07 15:12:19 EDT 1999 | Scott S. Snider
| I am interested in seeing how some of you calculate machine utilisation. Currently this was calculated off against the uptime. I really believe there is a better way of doing it i.e if I were to calculate this against machine's capacities. Any feed
Electronics Forum | Tue May 28 22:06:09 EDT 2002 | arcandspark
Two hours at 125 C will do nothing. IPC's new spec is 48 hours at 125C, the old spec I use to use for years was 24 hours at 125C. I do not have all the spec in front of me but if you reduce the temp to around 60C it can take up to 48 days. We use to
Electronics Forum | Tue May 28 22:06:18 EDT 2002 | arcandspark
Two hours at 125 C will do nothing. IPC's new spec is 48 hours at 125C, the old spec I use to use for years was 24 hours at 125C. I do not have all the spec in front of me but if you reduce the temp to around 60C it can take up to 48 days. We use to
Electronics Forum | Wed Jun 25 12:48:51 EDT 2008 | sleech
I would love to see the documentation of the experiment that indicated that a 24-hour/70 degree C bakeiing cycle at 10Pa is more effetive than a 24-hour 125 deg C baking cycle at normal atmosphere. We have looked at the old Levey-Perlmann paper and f
Electronics Forum | Tue Oct 29 04:40:42 EDT 2019 | jags
how long i can keep pcba after bottom reflow soldering to top side reflow soldering. like 12 hours or 24 hour or 48 hours........Enig board. leadfree soldering with 10% flux
Electronics Forum | Fri Aug 18 20:42:02 EDT 2000 | KYUNG SAM PARK
Hi. Smtguys I need help. The delamination of smd (QFP) occured when we checked with the SEM. This device have been excursed smt process after baking for 24 hour (125��) in oven. Are there any other reasion in SMD delamination except humidit
Electronics Forum | Fri Jun 23 14:23:20 EDT 2000 | Brian W.
We used to cure RTV3145 in an oven at 180 F for 2-4 hours Hope this helps, Brian
Electronics Forum | Thu Mar 15 17:28:44 EST 2001 | rentreo
Sounds like a problem I ran into recently. In my case it was a problem with via holes which were used as test points on our in-circuit tester. My problem was caused by moisture in the boards. My cure was a 24 hour bake at 100 deg c.
winsouce.jpg)