Electronics Forum | Mon Jul 27 13:26:00 EDT 2020 | lpbro
Get a gimbal for your phone to steady the shot. The video will look much more professional.
Electronics Forum | Mon Jun 26 00:22:26 EDT 2006 | YQ Deng
Through the pads of conncector(50pin) were printed full solder paste, the solder paste of about 2-5 pads follow to bottom of the connector 2-5 pins, the 2-5 pads outside of connector no any tin after reflow. Is this PCB problem? I can supply failur
Electronics Forum | Tue Dec 26 11:26:00 EST 2000 | acahill
If you have a known problem with the parts, then Reject them back to the Vendor. It appears that you have a solderability issue. As for Tombstoning on 0402 chips, this could trace back to the stencil design and/or machine placement. Define Tombstoni
Electronics Forum | Mon Jan 22 11:26:00 EST 2001 | marys
When adopting a new CIM system, it would seem that a large strain could be placed upon the IT department. When putting such a sytem in place, what can be expected interms of needs for the IT department? When planning such a move what changes should
Electronics Forum | Tue Apr 24 20:26:00 EDT 2001 | kcw
We solved similar problems some time ago. Check the volume dispensed or printed. Also check that the glue or solder paste has not expired and if in doubt use a new cartridge or change supplier. Ensure the Z axis stroke and placement force is corre
Electronics Forum | Thu Nov 26 00:34:30 EST 1998 | Brian G.
Certain board designs require the unavoidable use of non-plated holes and slots. Presently, this requires a trip back to the drill house to open up the aforementioned holes, to remove the unwanted plating. In situations requiring non-plated holes and
Electronics Forum | Fri Mar 26 00:33:32 EST 2004 | alwil
I'm keen to find out more about the SAWA cleaner. What type of solvent is being used. Does anyone use water or any other enviromentaly friendly agent. Is the result with glue stencils good.Is this a messy machine to use. Any feedback would be good. I
Electronics Forum | Tue Jun 15 09:26:00 EDT 2004 | johnthor
There was a thread in the IPC TechNet a few days ago about this subject. Basic conclusion was that there is a reliablility concern if the lead free balls don't reach liquidus with the Pb profile. Haven't tried it myself. John Thorup
Electronics Forum | Tue Oct 26 00:49:42 EDT 2004 | pilengr_tw
Yes, we have an SOP on how to measure. Basically, calibrate the measuring device and measure tension on the 4 sides and one at the center of the stencil. All measurement should be within 30 ~ 50 N/cm otherwise we will not use it and return it to sten
Electronics Forum | Mon Jun 13 04:26:00 EDT 2005 | Joris Groot koerkamp
For the lead free reflow process we tested with our Vitronics 500smr oven. To reach the high temperature of the lead free profile was no problem. We are not using an active cooling system so the pcb's are maby to hot wen the leaving the oven. Can an