Electronics Forum | Tue Nov 17 15:27:20 EST 1998 | Barry Kauffman
Can someone please tell me where I might find detailed information on the processing of a double-sided flex circuitry design. I am looking for specifics such as methods of fixturing,printing,placing and reflowing.Things to keep in mind when processin
Electronics Forum | Tue Aug 08 21:00:24 EDT 2000 | Dave F
Shawn: You're correct most solder preform manufactures don't want to sell preforms without skinning you alive for tooling charges!!! Considering alternatives, can you print or dispense paste? It would be mucho cheaper. We've talked about using pa
Electronics Forum | Thu Nov 19 17:36:03 EST 1998 | Christopher Lampron
| Can someone please tell me where I might find detailed information on the processing of a double-sided flex circuitry design. I am looking for specifics such as methods of fixturing,printing,placing and reflowing.Things to keep in mind when process
Electronics Forum | Wed Jun 24 13:46:41 EDT 1998 | Chris Kelly
Brian, a couple of things really stick out here... 1) You are spraying what is referred to here at the CATT as "PINK DEATH" The 3355-11 is about the most active/aggressive flux you can get your hands on. I am concerned about both the condition
Electronics Forum | Mon Aug 09 12:46:59 EDT 2010 | ppcbs
Try tinning pads with a high pH water soluble flux like Kester 2331-ZX or Alpha Metals 3355-HB is what we use. It will remove the contamination quick;y without having to scrape with a blade. If you have a large number of bare boards you can run them
Electronics Forum | Mon Jul 20 20:58:54 EDT 1998 | Dave F
| | Dave: | Wayne is correct with his analysis of ultrasonic spraying - we also use Sonoteks. However, your post didn't ask for a different system, just a clarification regarding your problem. What type of flux system are you currently using - s
Electronics Forum | Mon Jul 20 20:58:49 EDT 1998 | Dave F
| | Dave: | Wayne is correct with his analysis of ultrasonic spraying - we also use Sonoteks. However, your post didn't ask for a different system, just a clarification regarding your problem. What type of flux system are you currently using - s
Electronics Forum | Wed Jun 24 11:59:31 EDT 1998 | Brian Conner
| What is your current solder pot temperature? Whatever that temperature is, | has it been verified/calibrated? | What kind of flux is being used? No-clean, OA, RMA? | How is the flux being applied to the PCB? | Is this problem occuring on ALL nega
1 |