Electronics Forum: 4-5 0 (Page 14 of 24)

Topaz X Head Optimization

Electronics Forum | Tue Mar 06 17:24:31 EST 2012 | acsscott

OK, did some more testing this afternoon. First, I moved the LED’s from feeder location #23 to Feeder location 30. This is three down from the other component(#33) it is picking, so it should be able to hit them both at the same time for two of the

Underscreen cleaning cycles

Electronics Forum | Thu May 17 11:39:38 EDT 2012 | stentech

Hi again quickly. Anyone need a sample let me know ..no charge. I would be evry interested in your findings and can give many references for you to talk to..customers. Scott I am working on a project with different cut parameters very time consuming

assembly software for JUKI

Electronics Forum | Wed Jul 03 09:13:23 EDT 2013 | dontfeedphils

I currently run the HLC software suite with a 750/760 line and another 2060 line. For the 750/760 line I have to stick with the older HLC, version 4.5 I believe, which I actually run inside of a Windows 98 virtual PC using a dongle emulator. The 20

H49s crystals been placed

Electronics Forum | Tue Jul 30 15:04:54 EDT 2013 | ericrr

Is it just possible that H49s crysats are hard to place, so it looks like it has been place by a perfectionistic instead of looked like it had a parachute type loading. This is the H49 short stubby type crystal about 10 mm long (width) about 4.5 mm

Shoot Up Reflow Zone

Electronics Forum | Thu Dec 08 13:34:46 EST 2016 | spitkis2

We are currently experiencing with our SMD Solder > Reflow Equipment on Shooting-Up Zones (Zones > 3,4,5,7 & even Cooling Zone). PV exceeds about > 5-10 degrees with the SP. (ex: SP=140deg, actual > PV = 145deg & higher). Our equipment undergo a

Re: Wave Solder Problems - VIA HOLES

Electronics Forum | Mon Jun 07 12:22:44 EDT 1999 | Chrys Shea

| I'm encountering a new problem at my new company that I haven't encountered before in my past life - and that's Wave Soldering VIA holes. | | We've been getting a rash of defects that we call in this company, "insufficient solder in VIA hole." The

Sn/Pb diffusion

Electronics Forum | Mon May 20 21:29:52 EDT 2002 | davef

Q1: Are we saying then that IMC can occur at the solder / Cu pad join on the PCB when finished assembled? A1: Yes, but in a broader context I am saying that when someone solders correctly, they form an IMC. Q2: Will the tin diffuse with the Cu over

Re: Ceramic + Hi-temp solder

Electronics Forum | Thu Apr 22 08:43:25 EDT 1999 | Michael N.

| | I'm having problems with trying to get a good solder joint using a Ceramic PCB. We are using AMTECH hi-temp solder (ws-486 96.5/3.5ag). My profile looks great and I used the recommended profile from Amtech with a few adjustments. My max temp is a

Foam fluxer maintenance, storage and cleaning

Electronics Forum | Mon Nov 09 09:44:22 EST 2015 | davef

Purpose. This describes setting-up a wave soldering system set-up for a new assembly design or checking a wave solder machine operation with a test board. Applicability. To be used for new design printed circuit assembles and during machine accept

expired solder paste

Electronics Forum | Thu Apr 03 22:56:48 EDT 2008 | davef

Potential impacts of using expired solder paste are [University of Bolton]: * Changed paste rheology. Result: poor print quality * Loss of solvents. Result: reduced flux activity * Changed flux formulation. Result: More difficult to clean flux residu


4-5 0 searches for Companies, Equipment, Machines, Suppliers & Information

Thermal Interface Material Dispensing

Nozzles, Feeders, Spare Parts - Siemens, Fuji, Juki, Yamaha, etc...
2024 Eptac IPC Certification Training Schedule

Wave Soldering 101 Training Course
Hot selling SMT spare parts and professional SMT machine solutions

High Precision Fluid Dispensers
2024 Eptac IPC Certification Training Schedule

Best Reflow Oven