Electronics Forum | Fri Jul 08 12:54:02 EDT 2005 | Roberto Rodriguez
I have a omega meter 600 SMD, but I need a calibration Certificated and Service Support, I'm tring to find in Internet but this machine is OLD. Do you know a company give this Service? Please contact to Email. Roberto.Rodriguez@Teradyne.com Eng. Ro
Electronics Forum | Tue Nov 02 15:48:23 EST 2004 | Mike
Hi I am the Sales Mgr. for a Circuit board shop in Plymouth,MN Check out our Web site; http://www.circuitscience.com any questions please call or email me, Mike Dupont 763-559-9515 Tel 763-559-2569 Fax. miked@circuitscience.com
Electronics Forum | Thu Sep 01 18:27:28 EDT 2005 | Board House
Hi I currently Manufacture product for Dataradio Inc. in Quebec. and would be interested in quoting your product. We are a Multi-layer facility in Minnesota, we currenty manufacture layer counts between 2 & 18 layers. Line widths and Spacing down t
Electronics Forum | Tue Jun 15 12:54:34 EDT 2004 | jsmith01
It seems like the break is happening between the sn and ni. The parts are dull in appearance will not take solder even with an iron after they come off so it leads me to believe that there is only ni left on the part. The parts are liquidous for ab
Electronics Forum | Mon Aug 21 20:20:18 EDT 2000 | Dave F
Hi CJ: I guarantee you that the portions of you BGA that will physically move the most as a result of changing temperature are the corners. For this very reason, many BGA have BT substrates that have a tg of 210�C. I would demonstrate the potentia
Electronics Forum | Thu Sep 01 18:53:08 EDT 2005 | Board House
Pr. I agree with some of the above responses. if you are seeing Delam issues with incoming PCB's the following should be check. 1) Check the OEM Print to what Material they are calling out to be manufactured with. 2) If they are calling out for S
Electronics Forum | Thu Aug 17 22:22:29 EDT 2000 | C.J. Long
Hi erverybody: I am from a PCB shop. One of our product is with 19 X 19 ceramic BGA and my customer is experiencing 0.1 - 04 % failure of open trace on cornoer BGA pad. Substrate is FR4 with TG 135 degree C and delta Tg is well below 3 degree C. Tra
Electronics Forum | Tue Apr 11 10:30:46 EDT 2000 | Jeremy Smith
I am having a problem with some joints on a 100 pin pqfp and few different soics on one particular board. When viewed a 8x with a "Mantis" inspection scope the joints look as though they wetted to the ic leg but when probed the leg will pop loose.
Electronics Forum | Thu Feb 18 17:49:28 EST 1999 | Ryan Jennens
Hey all- My question is this: My stencil printer operator has said that he has to wipe our 6-mil stencil each pass to get the paste in the 20-mill pitch aperatures for a QFP to release well. We are using Amtech NC-559 type 3 paste with 89.5% metal
Electronics Forum | Tue Aug 09 11:57:11 EDT 2005 | Board House
Hi Ted, I am a Sales Manager for a Circuit board Manufacture in MN. We have seen the Majority of our Customer base switch to Enig do to shelf life issues of silver and Tin. Silver, Tin & OSP all have a shelf life between 6 - 8 Mos. Enig is betwee
winsouce.jpg)