Electronics Forum | Thu Apr 22 17:19:57 EDT 1999 | JohnW
| | We process both tin/lead plated boards and gold plated boards in our surface mount group. I have used Sn62/Pb36/Ag2 solder paste on all gold plated boards to help prevent gold scavaging. To reduce the amount of different solder pastes we have t
Electronics Forum | Tue Aug 31 21:45:49 EDT 2004 | KEN
I have experienced this directly in SMT and wave solder. Fillet lift (can) be a direct indicator to lead enrichment (but its not the exclusive symptom). Lead enrichment in smt joints reduces the interfacial strength shortening the time to creep f
Electronics Forum | Mon Apr 23 15:44:31 EDT 2007 | flipit
Steve, You read it the same way I read it. Some of my coworkers thought that the 600 micron and under spec meant that you could use lead solder and be exempt at this component pitch. That is why I posted it on SMTNET. The exemption specifically s
Electronics Forum | Wed Apr 25 15:19:15 EDT 2007 | flipit
Steve, See the link below. See the out take from the link below. http://forum.europa.eu.int/Public/irc/env/rohs/library?l=/requests_exemptions/resistant_applications/hpdoc/_EN_1.0_&a=d The specific verbiage is, "This exemption request seeks to
Electronics Forum | Fri Aug 07 07:52:15 EDT 1998 | Earl Moon
| | Is there any problem using SMT on gold boards? 15 years ago we were told not to use gold boards, but I can't remember why. Judging by the other postings it now appears to be common. Only problem I see is that the nickel should be plated, not e
Electronics Forum | Mon Aug 10 21:52:34 EDT 1998 | Dave F
| | | Is there any problem using SMT on gold boards? 15 years ago we were told not to use gold boards, but I can't remember why. Judging by the other postings it now appears to be common. Only problem I see is that the nickel should be plated, not
Electronics Forum | Tue Aug 11 07:51:57 EDT 1998 | Earl Moon
| | | | Is there any problem using SMT on gold boards? 15 years ago we were told not to use gold boards, but I can't remember why. Judging by the other postings it now appears to be common. Only problem I see is that the nickel should be plated, n
Electronics Forum | Wed Aug 12 07:22:52 EDT 1998 | Earl Moon
| | | | | Is there any problem using SMT on gold boards? 15 years ago we were told not to use gold boards, but I can't remember why. Judging by the other postings it now appears to be common. Only problem I see is that the nickel should be plated,
Electronics Forum | Mon Mar 01 12:50:47 EST 1999 | justin medernach
| Hello! SMT professionals, | | I do not know if anyone posted this question before. | Last week, I reflowed our newly designed thin Rigid-Flex pcb with 0.040" thickness. I found all of pins of a TQFP48 ic did not get wetted. I could see on the hee
Electronics Forum | Fri Sep 17 06:01:12 EDT 1999 | Earl Moon
| | We have some SMT components with gold plated leads. They're actually LCC led packages. A good solder alloy to use would be Indium / Lead to reduce tin dissolution into the gold and avoid the resultant brittle intermetallic compound. However, a re
Main Products: 1. Original new and Original Used SMT/AI Spare Parts. 2. SMT Equipments And Related Machine( SMT Calibration, SMT Feeder Carts,Conveyer etc.) 3. Maintenace and Repair Service Pre-Sales Service Provide details ab
Manufacturer's Representative / Manufacturer / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
Building A, Jiepeng Square, Fuyong
Shenzhen, 30 China
Phone: 0755-33578694