Electronics Forum | Fri Feb 18 11:25:14 EST 2005 | davef
It's weird that it would be just 0805. When we see this it relates to a single part number and it goes way after a time. We use a Humiseal 1B73. I've emailed you the contact for a person that is very knowledgeable on conformal coatings.
Electronics Forum | Mon Aug 09 07:13:08 EDT 2010 | raghu
We have PVA 354Bench top conformal coating machine. We are going to procure the Humiseal 1B31 material. Is this material is suitable for this model of machine? Is there any special pecautions to be taken while programming? What are the main problemsd
Electronics Forum | Tue Aug 10 01:02:31 EDT 2010 | raghu
We have PVA 354Bench top conformal coating machine. We are going to procure the Humiseal 1B31 material. Is this material is suitable for this model of machine? Is there any special pecautions to be taken while programming? What are the main problems
Electronics Forum | Thu Nov 23 06:05:24 EST 2006 | 1B73
The solid content of 1B73 is too low, especiall when you add large amount of thinner, not easy to get enough coating thickness.
Electronics Forum | Thu Jul 03 17:29:42 EDT 2008 | mikesewell
Re: item 3 - there are ultrasonic thickness machines (Panametrics makes one) that can measure coating dry with a small transducer head. A little pricey for ones that measure reliably in the .003" +/- .002" range.
Electronics Forum | Tue Feb 18 11:06:49 EST 2014 | cunningham
Does anyone do this? We have a small booth and lots of different kinds of media to try. it will be local stripping of coating on components for rework purposes. My main concern is ESD levels and how best to measure this. Any ideas or any papers o
Electronics Forum | Wed Feb 19 06:20:05 EST 2014 | bandjwet
These micro ablation stations can be outfitted with air ionizers and you can use less electronegative materials like corn starch as the blast media. Laser ablation works on parylene and other coatings when on metal surfaces. BWET
Electronics Forum | Thu Mar 31 10:14:06 EST 2005 | davef
There's some nice low-VOC uV coatings out there. We don�t use uV cured coatings, but try: * http://www.emersoncuming.com * http://www.dymax.com * http://www.mgchemicals.com * http://www.loctite.com * http://www.humiseal.com Be aware that uV co
Electronics Forum | Wed Mar 04 10:23:03 EST 2015 | rgduval
I haven't used this particular CC, but...found this in their data sheet: "AVR 80 BA Conformal Coating will be touch dry after 15 - 20 minutes at room temperature and does not require a thermal cure. The full properties of the coating will be obtaine
Electronics Forum | Fri Feb 18 10:10:49 EST 2005 | Frank R.
Thanks Dave, The problem is on all 0805. Do you think it could be a reaction with the flux from the wave or the one in the paste. Do you think the problem is the viscosity of the coating. SPEC = Viscosity 150cP nominal ASTM D-1384. I ask you all