Electronics Forum | Fri Apr 05 15:24:14 EDT 2019 | sever_83
What can cause solder balls to appear after conformal coating? Using Dymax 9-20557, light curing for 1.5 mins. Can too much heat from light cure cause solder balls?
Electronics Forum | Fri Jan 05 12:01:26 EST 2001 | Jim M
I've been involved with no-clean flux and conformal coat in the past.It has been my experience that the amount of no-clean flux used is proportionate to how well the conformal coat adheres to the boards.No clean paste did not affect adhesion. The co
Electronics Forum | Fri Feb 13 14:50:57 EST 2004 | blnorman
Underfills could improve reliability. If you pick materials right, you could co-cure and underfill and coating.
Electronics Forum | Mon Jul 02 08:57:21 EDT 2012 | dontfeedphils
It'll probably help to know what type of coating you're using on your boards, how it's being applied, and how it's being cured.
Electronics Forum | Tue Jul 03 03:12:20 EDT 2012 | mccabekev
Unfortunately our customers expect this coating on the boards so that is not an option. There must be something that can mark underneath without washing off. The silk screen doesn't wash off
Electronics Forum | Tue Jul 03 03:13:14 EDT 2012 | mccabekev
Unfortunately our customers expect this coating on the boards so that is not an option. There must be something that can mark underneath without washing off. The silk screen doesn't wash off
Electronics Forum | Tue Sep 06 12:41:52 EDT 2016 | kmclain
IPC J-STD-001 does not allow solder inspection to be combined with coating inspection for classes 2 and 3.
Electronics Forum | Wed Jan 27 09:00:56 EST 1999 | Chris Fontaine
| | I have boards coated with Humiseal 1B73. At a late point mfg. site we need to remove a series of 0603 resistors for optioning purposes. I have been trying to determine the fastest, easiest way to re-coat the pads after removal. Drying time of the
Electronics Forum | Sat Jan 23 07:08:54 EST 1999 | Graham Naisbitt
| I have boards coated with Humiseal 1B73. At a late point mfg. site we need to remove a series of 0603 resistors for optioning purposes. I have been trying to determine the fastest, easiest way to re-coat the pads after removal. Drying time of the c
Electronics Forum | Sat Jan 06 10:24:33 EST 2001 | Dave F
Some NC fluxes work well with conformal coatings others do not. Your coating materials supplier should be able to help. If they can't you're talking to the incorrect person. Try our friend Graham.Naisbitt@concoat.co.uk www.concoat.co.uk CONCOAT Lt