Electronics Forum | Wed Nov 26 09:16:59 EST 2008 | barryg
Hello everyone, after a short layoff I am glad to be back. I have a question. I have a button (snap button) that is being soldered to a strip of sac coated copper. We are questioning the joint strength of this from our vendor as we see these popping
Electronics Forum | Wed Nov 26 11:19:58 EST 2008 | vladig
I don't think you can find any specs on that. As long as a solder joint can not be broken by virtually "blowing over it" any reading on the UTS, or shear strength can be very confusing. You can specify, though that the assembly (joint) should withsta
Electronics Forum | Wed Mar 30 16:07:24 EST 2005 | Dreamsniper
If there's no shear strength standard for solder joint, how will I define my pad width and length then. I have a 8.5 mils width and my component lead width is 8.66 mils based on manufacturer's minimum width specification. How will I identify that it
Electronics Forum | Tue Mar 29 14:45:12 EST 2005 | davef
IPC-TM-650 TEST METHODS MANUAL Number 2.4.21.1 Subject: Bond Strength, Surface Mount Lands Perpendicular Pull Method 1 Scope This test method is used to determine the bond strength (breakaway strength) of surface mount lands from substrate materials
Electronics Forum | Thu Mar 24 19:19:17 EST 2005 | EA
Hi davef, Appreciate your advise......
Electronics Forum | Wed Mar 30 14:16:42 EST 2005 | chon
Davef That's why I mentioned that this was the "Closest" written procedure I've found related to this type of tests.
Electronics Forum | Mon Apr 04 17:32:07 EDT 2005 | toromaster
we also have a need to measure the solder bond strength of our gull wing parts on our pwb. there are many published comparisons between eutectic SnPb and no Pb solders out there. the number that comes to mind is about 10N to 15N. I have not looked
Electronics Forum | Thu Mar 24 19:17:43 EST 2005 | EA
Hi, We are running the automotive product and question was throw to us how do we ensure that our solder joint are good enough after reflow.....and during the sealant process, there's a bit of bend on the nozzle and it toughes the component and custo
Electronics Forum | Tue Mar 22 03:23:10 EST 2005 | EA
Hi, We are trying to break a component ( SMT component ) off the printed circuit board and measure the quality of the solder joint. But, after breaking off and having the reading, we do not know whether the reading is it within the component specifi
Electronics Forum | Wed Oct 06 03:18:01 EDT 2004 | Joseph
Dear all, Recently our customer complaint that some components being came off from the pcba after dropping test.But the curious is, the leads show visible solder fillet covering more than 75% of termination area on pad, which is acceptable as per IP