Electronics Forum | Wed Apr 18 04:22:43 EDT 2007 | ray
I facing dewetting problem on Ag/Pd termination(chip component)during reflow process. The solder wetting is pull to terminal side and exhibits dewetting. Any one ever face the same problem and any solutions for the problem?
Electronics Forum | Mon Oct 22 21:34:36 EDT 2007 | davef
Double check on this, but we have this little voice in our heads telling us that your AgPd termination is intended for conductive adhesive applications. Check with your component supplier. We recall a thread on SMTnet [ http://www.smtnet.com/forums
Electronics Forum | Mon Oct 22 20:41:32 EDT 2007 | jkhiew
Hi Dave, The solder has tended to wet the component termination of Ag/Pd (chip capacitor) but has not wetted the pads, whereas the solder has wetted both termination & pads when using Ag/Ni/Sn finishes. Thks
Electronics Forum | Tue Oct 23 03:57:39 EDT 2007 | jkhiew
Thanks Dave. But I do not understand why the solder being wicking away by the component itself. Does Ag/Pd finishes has stronger wettability than LF HASL finishes ? Rgds
Electronics Forum | Wed Apr 18 06:18:53 EDT 2007 | pavel_murtishev
Good afternoon, Huh. My sympathy. We have the same issue. Check this: http://www.smtnet.com/Forums/index.cfm?fuseaction=view_thread&CFApp=1&Thread_ID=11637&mc=3 BR, Pavel
Electronics Forum | Mon Oct 22 10:51:48 EDT 2007 | davef
You say, "we have encountered solder wicking on components ..." We expect to see wicking on solder connections. Maybe we're just using different terminology. Please describe the problem that you're seeing.
Electronics Forum | Tue Oct 23 07:03:52 EDT 2007 | davef
We're not really sure. Usually when solder leaves the pads and wicks-up a component lead, it means the component lead is much warmer than the pad on the board. This is the direction we would have taken this if we hadn't taken the AgPd / conductive e
Electronics Forum | Thu Apr 19 16:54:32 EDT 2007 | flipit
I don't suggest using Pd/Ag or Ag/Pd terminated components unless you are forced to use them. You often see a line of demarcation that suggests a poorly wetted solder joint. I have had bad experiences with Pd/Ag terminated capacitors. Even when so
Electronics Forum | Mon Oct 22 05:04:08 EDT 2007 | jkhiew
Hi, Recently we have encountered solder wicking on components termination (total of 13 pcs of components on one pcb)with Ag/Pd finishes during lead-free reflow soldering. The pcb is LF HASL surface finish and LF solder paste composition is SAC305.We
Electronics Forum | Wed Apr 18 08:14:20 EDT 2007 | davef
Silver palladium termination * AgPd-terminated capacitors are designed for conductive adhesion. Reflow or wave soldering is not recommended. [EPCOS Multilayer ceramic capacitors, Soldering directions, October 2006] * CONDUCTIVE EPOXY BONDING. Epoxy c