Electronics Forum | Mon Mar 27 19:32:28 EST 2006 | PWH
You mention "large ground plane pads in the center". Could it be that these large apertures are allowing the blades to "dig" which somehow pulls paste from adjacent apertures as the blades recover?
Electronics Forum | Thu Feb 17 21:42:12 EST 2000 | Dave F
Hey Bud: Moved from that Bi-crap to something serious, eh? Several things: 1 Get in touch with Doug Romm (drom@msg.ti.com) at Texas Instruments. He talks palladium. 2 Review the archives on Palladium. 3 I think you're running light on temps. Eut
Electronics Forum | Thu Feb 17 21:42:12 EST 2000 | Dave F
Hey Bud: Moved from that Bi-crap to something serious, eh? Several things: 1 Get in touch with Doug Romm (drom@msg.ti.com) at Texas Instruments. He talks palladium. 2 Review the archives on Palladium. 3 I think you're running light on temps. Eut
Electronics Forum | Wed Mar 14 09:44:06 EDT 2007 | Cmiller
We use cartridges, that way nobody can mix back in paste off the stencil and no air can get in period. Any paste that is still good to use when removed from a stencil at the end of a job is put into a small pink zip-lock baggy with the date written o
Electronics Forum | Tue Apr 13 09:11:54 EDT 1999 | Dave F
| We process both tin/lead plated boards and gold plated boards in our surface mount group. I have used Sn62/Pb36/Ag2 solder paste on all gold plated boards to help prevent gold scavaging. To reduce the amount of different solder pastes we have to
Electronics Forum | Wed Mar 14 07:30:14 EDT 2007 | davef
So, you toss whatever is on the stencil every 8 hours. Correct? How long has it been on the stencil? * If that particular paste has been on the stencil for 8 hours, we'd agree to toss it too. * If paste has been on the stencil for less than 8 hour
Electronics Forum | Mon Mar 27 15:10:48 EST 2006 | ms
Hi Steve Thanks for your reply. Your comments make it sound like it may be the nature of this paste. Any one else agree? Paste control is fairly good. Paste is put in fridge straight after it arrives at inwards goods, (4deg). Removed from fridge
Electronics Forum | Thu Apr 22 17:19:57 EDT 1999 | JohnW
| | We process both tin/lead plated boards and gold plated boards in our surface mount group. I have used Sn62/Pb36/Ag2 solder paste on all gold plated boards to help prevent gold scavaging. To reduce the amount of different solder pastes we have t
Electronics Forum | Sun May 23 15:12:59 EDT 1999 | JohnW
| We are running a number of boards with 8-10 25 mil PQFPs on board. Our process is mature with at least 3 years experiance and statistically few opens on the QFPs. Our beloved purchasing department has chased the almighty $ and changed FAB vendor
Electronics Forum | Wed Aug 28 10:16:12 EDT 2002 | Jim M.
Sam We install a lot of die in the SMT room using same process as SMT parts.Water soluble solder paste is used for attachment of die to ceramic and boards. Biggest problem i found is the adjustment from installing the die in the bonding area. The t