Electronics Forum | Tue Nov 07 22:44:39 EST 2017 | wrander1
Hi I'm new to the world of wire bonding. I seem to have some sort of pad contamination Preventing gold wire from bonding to aluminum pats. There appears to be a dozen microns size particles. And a slight crackling of the surface at 500 X. I am send
Electronics Forum | Mon Aug 27 15:06:29 EDT 2001 | davef
This otta push Wolfgang over the top ... Recommended reading G.G. Harman, Wire Bonding in Microelectronics : Materials, Processes, Reliability, and Yield, 2nd edition, McGraw-Hill Electronic Packaging and Interconnection Series, 1997. G.G. Harman, R
Electronics Forum | Mon Jan 07 20:37:15 EST 2002 | davef
For soldered areas, we like to keep gold thickness substantially below the maximum you propose. Search the fine SMTnet Archives for our discussions on the topic of acceptable levels of gold with solder connections. Let�s fix this �no one seems be s
Electronics Forum | Wed Jan 09 17:14:48 EST 2002 | mregalia
Do you bond with Al or gold wire? What happens if the Ni is over 150 microinches? Thickness of nickel is one those things that we have not been consistent with. The industry seems to pretty much universally call for 100-200 microinches. Our old board
Electronics Forum | Fri May 29 07:17:02 EDT 2015 | anirudh_thabjul
Hiee everyone, I am a Hardware Engineer and also a PCB designer. I am using a Microntroller which is in "CHIP PACKAGE". So in order to connect our microcontroller with my PCB, i am using "Wire bonding Technology". So, Can any one suggust 1. whi
Electronics Forum | Fri Aug 17 01:40:55 EDT 2001 | V.RAMANAND KINI
We are in the watch & clock Business. We have a Watch IC chip that has to be wirebonded using Ultrasonic aluminium wedge bonder. The wire dia is 1.25mil. The PCB is made of G10 Glass epoxy copper clad laminate. The copper thickness is 18 microns. The
Electronics Forum | Fri Aug 17 11:55:31 EDT 2001 | davef
5uin. Your nickel thickness is fine. Although if you wanted to trade costs, consider giving-up nickel to 150uin thickness, while increasing the gold thickness. Gold over electroless nickel creates brittle joints because of phosphorous in the nicke
Electronics Forum | Fri Apr 17 21:46:18 EDT 1998 | Matthias Mansfeld
I plan to design a multichip module which contains 1 chip with about 200 pads and 2 chips with about 50 pads, no other components.The whole module shall replace as intermediate solution a single chip CPU in QFP208. Thus, the MCM itself must have t
Electronics Forum | Tue Nov 15 09:31:27 EST 2005 | arclightzero
I have been reading a good deal about IMC (purple plague in particular) in gold wire/aluminum pad wire bonds. My company uses ultrasonic wedge bonding, and for the most part all of our bonding is gold/gold, however we have one particulr part that has
Electronics Forum | Thu Sep 08 07:04:02 EDT 2005 | davef
Finer pitch: Wedge bonding can be designed and manufactured to very small dimensions, down to 50 mm pitch. Processing speed: Machine rotational movements make the overall speed of the wedge bonding process less than thermosonic ball bonding. Alumin