| | Hi, | | | | Help! Could anyone help to enlighten me on this? | | | | Question: | | | | If I have a CSP/BGA package of size X by Y and the standoff gap between the component and PCB is Z, What is the maximum allowable Y/Z or X/Z that using a n
Electronics Forum | Wed Sep 22 21:23:03 EDT 1999 | se
| | I've had some trouble pasting a test board for a MicroBGA trial. Most of the paste remains in the stencil apertures. | | The stencil is 6 mil thick, laser cut and electo-polished. | | The apertures are 12 mil in diameter with 20 mil pitch. | | We
Electronics Forum | Thu Sep 23 12:47:48 EDT 1999 | Earl Moon
| | | I've had some trouble pasting a test board for a MicroBGA trial. Most of the paste remains in the stencil apertures. | | | The stencil is 6 mil thick, laser cut and electo-polished. | | | The apertures are 12 mil in diameter with 20 mil pitch.
Electronics Forum | Tue Sep 07 12:02:30 EDT 1999 | Brad Kendall
| Dear sirs, | | If you have experienced Proflow of DEK screen printer, please let me know the details of it. | | Best regards, | | Jame Bond | | I have had Proflow for about 8 weeks now. I have had my fair share of problems with it. It does
Electronics Forum | Tue Jul 06 14:23:27 EDT 1999 | Earl Moon
| | | I've heard that use of VOC free flux with wavesolder fixtures can be challenging due to entrapment of water in the fixture. | | | | | | Is anyone out there successfully running VOC free with wave fixtures & did you experience problems? If so,
Electronics Forum | Thu Jun 24 18:24:13 EDT 1999 | Christian N.
| Dear guys, | | I have some problem on assembling micro-BGA with solder paste (63/37). The micro-BGA we assmeble is 0.75mm pitch and with 45 pin (solder bump is 96.5/3.5Ag). The stencil is a laser-cut stencil with 5 mil thickness. We are now usin
Electronics Forum | Fri Jun 25 09:51:35 EDT 1999 | C.K.
| Dear John/Earl | | Thanks for your clarifications. To me also the problem does not seem to be linked with the PCB. The Pre heater temp. is set at | 450 degree C. We are using Alpha Aq. cleanable flux. Can you elaborate on the Desired profilin
Electronics Forum | Sun Jun 20 16:58:31 EDT 1999 | Chrys Shea
| Has there anyone bold enough to try this in their shops? My cubemate just got through telling me that at his last shop, they had bare copper boards (no HASL, no OSP, no nothing), with minimal solderability problems. | Is your cubemate the same gu
Electronics Forum | Mon Apr 26 17:31:14 EDT 1999 | Earl Moon
| Hey MoonMan, | | Did I catch in one of your fabulous threads that you're using Tetra stencils? I'm anxious to find out how you're liking them. | | We we're all set up to go to Tetras, then mgt decided to close down our factory - Dooop! "Foiled"
Electronics Forum | Fri Apr 23 14:14:49 EDT 1999 | Chrys Shea
| Hi everybody, | | I would like to bench mark the quality out of our wave soldering m/c as far as DPPM levels are concerned. Can somebody provide me with some figures at their site or anywhere else for the same. | | Thanks | Upinder | ====== | We