Electronics Forum | Wed Jun 08 12:14:58 EDT 2005 | patrickbruneel
Could you describe the problem you encounter
Electronics Forum | Tue Jun 07 19:24:26 EDT 2005 | Joseph
Dear all, Recently we encountered some functionality failure when using lead-free component(Sn99.3/Cu0.7)at SnPb(Sn63Pb37) wave soldering process. Can lead-free component use at non-lead free process? Any input/idea are much appreciated. Rgds
Electronics Forum | Thu Jun 09 06:15:17 EDT 2005 | Clampron
Joseph, We have all been using lead free components for some time. Many passive already have a Pb free plating and we have not seen catastophic failures on them. From the information I have seen, I think this should be OK (with the exception of BGA'
Electronics Forum | Thu Jun 09 10:55:37 EDT 2005 | patrickbruneel
Hi Joseph, It's difficult to troubleshoot if the defect is unknown, but I agree with Chris The majority of components are already lead-free and only 17% of the worldwide electronics industry switched to lead-free wave and/or paste so the majority o
Electronics Forum | Thu Jun 09 05:04:05 EDT 2005 | Joseph
Dear Patrick, Unfortunately we do not know what exactly the failure as our customer refuse to reveal to us. From visual inspection the solder joints are smooth and shiny as per IPC-A-610 requirements. The component supplier (IR) commended that they
Electronics Forum | Tue Apr 24 21:00:58 EDT 2018 | marlonbc
Hi All, Would just like to course through this concern on a product that we are contracted to assemble. It is mainly used for an automatic hand sanitizer dispensing product. By design there is a restrictive value of current that it needs to dissipat
Electronics Forum | Tue Sep 10 08:24:45 EDT 2002 | davef
Most AOI discussion should include assessment of escapes and programming time.
Electronics Forum | Thu Jun 26 07:32:05 EDT 2008 | davef
Our operators enter and assess data into charts with limits determined by QA stats-types.
Electronics Forum | Mon Jun 28 12:09:17 EDT 2010 | davef
In 2002, the IPC released IPC 9850 for use in assessing placement machine performance.
Electronics Forum | Thu Feb 24 21:47:22 EST 2000 | Dave F
Interesting, Gary. Try this: 1 Assess candidate solders by reviewing J-STD-006 (http://canfieldmetals.com/j-std006.htm) to determine solder formulations that have liquidous temperatures in the desired range. 2 Request recommended profiles from supp
winsouce.jpg)