Electronics Forum | Wed Aug 07 11:07:14 EDT 2013 | garyck
On last question. Is it possible to feed loose resistors into the machine one at a time?. We use a lot of parts where yearly usage is less than 1000 per year. Gary.
Electronics Forum | Mon Aug 05 22:10:38 EDT 2013 | jaimebc
We have HRFT-301U ( staple bend) is fairly easy to set up. All you need is t-handle Allen that I believe is provided with the machine. All adjustments to form a part, both pitch and lead length are mechanically adjusted by sliding the forming and c
Electronics Forum | Mon May 06 16:14:41 EDT 2002 | russ
Would the lead finish on this part happen to be Paladium? I had a problem similar to this some time ago and we found the lead finish was not tin/lead over copper but paladium over nickel. We had to increase the reflow to 225 deg. C peak temp with t
Electronics Forum | Thu Jul 12 05:20:01 EDT 2018 | robl
We had the same issue recently, we swapped to a 2 part shield to allow AOI and SPC xray. We also tested using silver epoxy and putting a one piece can down after inspection. That worked too.
Electronics Forum | Wed Jul 11 06:14:21 EDT 2018 | uzbek
Hello, we are currently designing one device that needs shielding. Under the shield, there is one BGA chip and 0402 components. Now we have a dilemma whether we should go for a one-part shield or two-part shield. We talked with several EMS companie
Electronics Forum | Wed Dec 22 17:49:06 EST 2021 | mihai_voivod
I have this part: 142-1711-801 (Emerson). It is an SMT/TH part. https://www.digikey.com/en/products/detail/cinch-connectivity-solutions-johnson/142-1711-801/9992851 I want to reflow the part instead of hand soldering and/or reworking the solder jo
Electronics Forum | Mon Jan 30 03:42:49 EST 2006 | daxman
Thanks for the reply fellas, I spent all day today working on these machines, and indeed, this is bizzare. The main line was in production, and the placement was excellent on the CP6. I transferred a reel (400 parts per board) to the CP4 and the p
Electronics Forum | Fri Jan 14 23:31:35 EST 2022 | tey422
First of all, like I said before, I only worked on similar type of part. For this part, I would add at least 1 of 0603 size solder bead at each end (091845.jpg), 2 of 0402 size solder beads side by side would be even better.
Electronics Forum | Wed Feb 03 22:05:24 EST 2016 | mac5
Our company being an automotive supplier is all > about quality control, not a clean room > requiremen, This is a no clean process, all > surface mount boards and Solitec ovens. > Hopefully this answers your questions. Greg Hi Greg, Are you
Electronics Forum | Wed Oct 15 23:41:34 EDT 2014 | padawanlinuxero
Hello Chris I had a similar problem, what work for us was a combination of fluxer and preheat, we try different approaches what work was high pressure and a low traverse speed, and really heating up the upper part of the board, you see we need to u