Electronics Forum | Tue Nov 19 02:59:24 EST 2002 | yngwie
Hi Experts out there, pls help me with the following matters. How important is the bare PCB baking ? What is the temperature for baking @ what RH ? What would be the impact for the ENTEK finished board should the baking is really necessary ? For t
Electronics Forum | Thu Nov 21 14:17:27 EST 2002 | MA/NY DDave
Hi I can't give you the answer for your question because I have too many questions and would have to know a lot more before I was comfortable giving any advice. I have done mass Baking of piles of PCB's as a needed evil when piles of boards were ex
Electronics Forum | Wed Nov 20 16:53:18 EST 2002 | davef
Q1: How important is the bare PCB baking ? A1: Baking boards is a non-value added activity. Q2: What is the temperature for baking @ what RH ? A2: Search the fine SMTnet Arcives for bake recipes. Q3: What would be the impact for the ENTEK finishe
Electronics Forum | Fri Nov 22 08:57:56 EST 2002 | davef
Q1: What do you mean by "if the board is manufactured properly"? A2: If the epoxy is noy cured prooperly, for instance, the copper will not be well attached to the glass. So, peel strength will be lower. Q2: I don't believe that the peel off/or lif
Electronics Forum | Wed Nov 20 21:04:15 EST 2002 | yngwie
Hi Dave, What do you mean by "if the board is manufactured properly". If the board is not manufactured properly, humidity will have an impact on the peel strength? Is that what you mean. How does the Humidity impacted the peel strength ? Thru' which
Electronics Forum | Fri Nov 22 10:38:30 EST 2002 | slthomas
The follwing is from the Technet archives, per IPC's Jack Crawford. I dug it up during some investigation of a supplier's issues with humidity in an Asian plant: There is support for this in IPD-HDBK-001 w/Amendment 1 Handbook and Guide to Suppleme
Electronics Forum | Tue Oct 30 21:42:32 EST 2001 | surachai
I have question about board baking after in line washing machine then I would like to know some information that ; 1) Do we need board baking after in line washing machine? Both bare board and assembly borad normally we don't bake . 2)In case of ne
Electronics Forum | Sat Apr 25 09:13:26 EDT 1998 | Earl Moon
| Hi, | A collegue of mine, working on incoming inspection | departement, asked me if I know any good standard,preferrable | on CD-ROM with high-quality images of different defects | that can be found on bare pcb`s. | I know IPC-standards, but i
Electronics Forum | Thu Aug 24 15:54:13 EDT 2006 | davef
It depends. What is: * Storage environment and period * Board laminate, epoxy, and copper thickness of PTH * Down stream process * Etc FR4 0.062" thick boards absorb between 0.08 to 0.1%Wt of moisture within a 24 hour period, and 0.2 to 0.23%Wt in
Electronics Forum | Tue Mar 17 10:47:56 EDT 2020 | davef
IPC-1601 covers PWB bake-out, methods for determining optimum bake time and temperature, caveats for certain PWB plating finishes, etc. IPC-1601 is to bare boards as J-STD-033 is to components
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830
.gif)