Electronics Forum | Tue Nov 15 22:27:21 EST 2011 | Jacki
Hi Zaza Thanks. Again, very appreciate if you advise me where I can get the SN100C solder bar that is water soluable. Now I'm checking Nihon Superior(Singapore) whether they have or not. As our customer's preference, we have to use the watersoluab
Electronics Forum | Thu Dec 29 22:19:36 EST 2005 | Joseph
We have tested SN100C for LF wave soldering process since August'05 and currently start production for a month ago. Initially we use SAC305, but due to the shrinkage cavities (micro-crack) we changeover to SN100C. In summary, SN100C did perform well
Electronics Forum | Wed Jan 04 17:06:20 EST 2006 | samir
All I can say about Alpha and their GOTT-DAMN website is THEY SUCK!! I refuse to register to view product literature... for that reason, Alpha Metals, you won't be looked at for my pb-free paste or bar solder evals.
Electronics Forum | Thu May 25 19:21:58 EDT 2006 | grantp
Hi, So that's really important to have a specific flux for lead free? We are looking at changing to SN100C after reading this thread and other stuff we have found, so can anyone recommend the best no clean flux for that metal? Do you need differen
Electronics Forum | Thu Dec 29 09:20:30 EST 2005 | Cmiller
We have tested SN100C and SAC305 in our selective solder machine (Ersa Versaflow). We wanted to test both alloys in the selective first because the investment in filling the pots is minimal. In our initial tests the SN100C alloy appears to be the bes
Electronics Forum | Wed Jan 18 17:07:32 EST 2006 | gregoryyork
Sorry Bob Could not respond been away busy. Just to correct you, we did not copy the SACX as we brought ours to market at least six months before so how could we copy, it is also a little different, but nicely reassuring when the 'big boys' do some
Electronics Forum | Wed Jan 04 08:32:21 EST 2006 | GS
HI aj, I suppose you have visited the Alphametal situ where they have plenty of information about SACX http://www.alphametals.com/main.asp For sure every one talks well about own products. I think the best judgement can be done from those who h
Electronics Forum | Thu Jun 28 09:54:06 EDT 2012 | mosborne1
Dave, They rework fine. All solder joints on the whole board look great especially for lead free sac305. Here are the reflow specs: SAC305 no clean solder paste – Kester EM907 Kic thermal profiling device – 50%process window green light profile. • M
Electronics Forum | Fri Apr 07 17:44:07 EDT 2006 | ratsalad
I still have half of a 500 g jar of this paste left. I'm going to give it another shot, but my first experience was not so wonderful. Everything was great until we reflowed it. Our profile matched AIM's recommendation, as far as I can see. The ch
Electronics Forum | Mon Dec 03 16:05:55 EST 2012 | emeto
Hi all, We are going to evaluate new LEAD-FREE solder paste. We stopped our attention on 3 manufacturers but the variety of products is so big. What would you recommend for a daily basis use? Is SAC305 the most commonly used alloy? We are a subcontr