Electronics Forum | Tue Sep 30 21:00:41 EDT 2003 | davef
We're not clear on what you seek. So, as a starting point for our discussion, we wouldn't get agitated if we saw "routine" coplanarity of 4 thou. For instance: Maximum Lead Coplanarity [Altera] Package||Acronym||Lead material||Finish||Maximum Lead
Electronics Forum | Fri Dec 12 01:06:02 EST 2003 | kenny
Dear folks; I am currently looking a PCB manufacturer who can fabricate PCB with the following specification:- Board sizes: _20000__ x _20000__ mils Thickness: 125 mils PCB material: FR4 Surface finish: 30 microinches Gold over 200 micro inches Nic
Electronics Forum | Thu Jan 22 15:51:08 EST 2004 | solderboffin
CBGA devices are a bit trickier to reball than run of the mil plastic devices. Once assemblied they are a bit like a sandwich when fitted to a PCB. From top to bottom it goes BGA device - Eutectic solder - High temp solder ball - eutectic solder -
Electronics Forum | Tue Feb 03 06:52:45 EST 2004 | paul_bmc
About 2 years ago our company tried to go with a post reflow AOI inspection. This AOI was suppose to be able to inspect to a level class 3 product. **It is impossible** You cannot inspect for a heel fillet and inspecting for poor wetting is a very
Electronics Forum | Thu Jan 29 15:30:41 EST 2004 | pjc
Rick, As I understand your comments, you do not need to clean off the flux residues? Then hot water and a little cleaning chemistry should do. However, there may be some reaction by the residual flux if not enough cleaning chemistry is used. There a
Electronics Forum | Tue Feb 17 04:52:13 EST 2004 | John W
There's normally a number of reasons people want to know what melts 1st, 1 - to see if you know, 2 voiding issues - whole can of worms 3 device alignment. One of our collegues has said that most balls are Eutectic, that's in fact not totally correct.
Electronics Forum | Wed Mar 24 21:51:23 EST 2004 | davef
Dreamy It sounds like you are having fun in your new job. Saponifier. Alkaline chemicals, added to water, that convert rosin/resin flux residues in the water to soluble soaps. Generally, saponifiers are better if used in an aggressive spray-in-ai
Electronics Forum | Tue Apr 13 22:48:11 EDT 2004 | Ken
I assumed the balls were tin/silver 221C or tin/silver/copper 218C liquiduous....but, this is obviously not the case. It looks like you balls are almost pure tin (mp=238C) You are correct. This is exactly the same as using 10/90 high temp balls o
Electronics Forum | Thu Jun 10 16:23:11 EDT 2004 | davem
Hi Grant, In previous positions I've had experience with the Fuji CP43, CP6, CP642, CP643, CP65, IP3 & QP242. In operating, training and process engineering capacities. Presently, I'm working with 2 SMT lines (in a process engineering capacity) wit
Electronics Forum | Mon Jan 09 18:51:05 EST 2006 | grantp
Hi, I have used both MYDATA TP9, MY9 and more recently MY12. MYDATA machines are just not accurate, and we did everything possible, and every kind of upgrade they had. We ended up putting in Fuji XP based machines, and the differences are very notic