Electronics Forum | Thu Sep 12 01:49:28 EDT 2002 | ck
Hi all, Any stencil opening recommendation for 20mils pitch mirco BGA. Currently, using 12mils round opening, 5 mils thickness. Seen to have weak joints as it crack after Ict testing. thks
Electronics Forum | Thu Sep 12 09:15:29 EDT 2002 | mhoughton
I have printed and placed similar devices in high volume with exactly this spec for a couple of years with no problems, are you using laser cut stencils and what type of solder paste are you using? and what is the end use of the product as it may nee
Electronics Forum | Thu Sep 12 09:12:22 EDT 2002 | mhoughton
I have printed and placed similar devices in high volume with exactly this spec for a couple of years with no problems, are you using laser cut stencils and what type of solder paste are you using? and what is the end use of the product as it may nee
Electronics Forum | Thu Sep 12 10:45:29 EDT 2002 | pbarton
We have used a laser cut stencil 0.15mm (0.006") thick with 0.3mm (0.012") square apertures radiused in the corners 0.06mm (0.0025") to aid paste release. This approach with the (type 3) paste we use has proven successful on thousands of devices plac
Electronics Forum | Thu Jun 18 14:25:21 EDT 2020 | sara_pcb
We have observed Plastic BGA crack in encapsulation to substrate interface. After reflow, the device was not functioning. The Crack is observed in the fresh lot during visual inspection. What is the attachment process of package to substrate? where c
Electronics Forum | Mon Sep 15 06:14:49 EDT 2008 | milas
Hi Has anyone experienced laminateand BGA cracking on ENIG finish boards built using a lead free process? The laminate is cracked directly underneath the pad where the solder joint has cracked. We have confirmed the cracking via Microsectioning. We
Electronics Forum | Mon Nov 27 08:05:50 EST 2006 | davef
There is no standard for a strain gage measurement of allowable deflection of a board or a fixture. It's possible that your fixture is causing the BGA cracking that you see. What protion of the BGA is cracking? If it is the solder connection, sear
Electronics Forum | Thu Sep 18 13:55:48 EDT 2008 | vladig
Any crack in laminate caused by excessive flexure would look exactly like the one in the image. Vlad
Electronics Forum | Wed Nov 29 01:12:12 EST 2006 | callckq
Dear Davef, Thanks for your input...The crack happen at the pad/solder ball interface..Pls review the new thread that I post just now with title called "BGA BALL CRACK AT PAD/SOLDER BALL INTERFACE" Thanks!
Electronics Forum | Tue Sep 16 22:29:25 EDT 2008 | davef
Would you attach pix of the sections?