Electronics Forum | Wed Sep 11 16:57:04 EDT 2002 | bigwop
I've seen this problem caused by the cool down. > On a 7 zone oven I made a profile to peak at zone > 5 to give some semblance of control to the cool > down. The component can develope a big delta T, > because of the difference of materials Che
Electronics Forum | Wed Sep 11 13:20:37 EDT 2002 | stepheno
I've seen this problem caused by the cool down. On a 7 zone oven I made a profile to peak at zone 5 to give some semblance of control to the cool down. The component can develope a big delta T, because of the difference of materials
Electronics Forum | Wed Sep 11 23:20:44 EDT 2002 | scottefiske
Profiles are absolutely the first course of action to validate. A few additional questions would be: * Moisture can cause warping as well, verify the manufacturers recommended handling procedures were followed. * Where is the suspect BGA located
Electronics Forum | Thu Sep 25 17:35:28 EDT 2003 | denis
To be precise, the component is a Xilinx Virtex platform FPGA with 1152 balls. We also assemble some DSPs up to 1000 balls with metal cover. At best, we can remove the components but it is almost impossible to find a working solder profile using IR.
Electronics Forum | Tue Jul 28 02:22:59 EDT 1998 | Bob Willis
Here is what I would do faced with your problem. First I would profile a similar board or use an existing profile. From there I would place the dummy device on the surface of a sample board with a thin thermocouple soldered to the board surface under
Electronics Forum | Sat Jun 09 00:53:34 EDT 2001 | ianchan
Hi Folks, My Production runs a uBGA-liken product, and uses Pallets to support the 0.8mm thick pcb, during the SMT + reflow oven process. Process/QA see occurs: 1) 0402 unsolder? 2) 0402 tombstone? 3) "uBGA" poor-visual joints (dry joints)? Took
Electronics Forum | Mon Jul 27 13:59:11 EDT 1998 | Robert Steltman
We are about to run our first BGA devices and would appreciate some confirmation on a few points. First some details: PCB & Device: ============= 1) 16 layer (4 power, 4 gnd, 8 signal) 2) gold on nickel finish 3) ceramic BGA with eutectic balls Refl
Electronics Forum | Tue Jul 28 17:37:00 EDT 1998 | Robert Steltman
| Here is what I would do faced with your problem. First I would profile a similar board or use an existing profile. From there I would place the dummy device on the surface of a sample board with a thin thermocouple soldered to the board surface und
Electronics Forum | Tue Dec 28 12:55:16 EST 1999 | Justin Medernach
Greg, The best advice that I can give you is a PBGA will respond just like any other surface mount package. There may be a 5 degree delta between a PBGA 356 and a QFP208 but the two respond very similarly in the convection reflow environment. CBGAs
Electronics Forum | Tue Jul 28 02:13:57 EDT 1998 | Bob Willis
There is a procedure for profiling on my web site that may be of use to start with www.bobwillis.co.uk | We are about to run our first BGA devices and would appreciate some confirmation on a few points. | First some details: | PCB & Device: | ======