Electronics Forum | Fri Jun 19 18:44:23 EDT 1998 | Steve
Does anyone have wave solder experience using OSP and VOC free no clean flux?
Electronics Forum | Fri Jun 19 19:07:07 EDT 1998 | Earl Moon
| Does anyone have wave solder experience using OSP and VOC free no clean flux? Well, Steve you back in action. Yes, it works fine. Earl Moon
Electronics Forum | Wed Oct 02 15:20:55 EDT 2002 | Eric
Is there a steadfast rule of thumb for a good solder joint on an Enig Gold board. I come across this number 217C when discussing BGA profiles. Is this a published number? I sure could use a reference. Anybody feedback is appreciated.
Electronics Forum | Wed Oct 02 16:13:05 EDT 2002 | babe
Have you had your solder pot tested? I find that levels of contaminants can rend a solder joint that dull look.
Electronics Forum | Thu Sep 26 14:43:43 EDT 2002 | Jim M.
unsure of what solder spec. your working to?.IPC/EIA J-STD-001C, Section 9.2.4 clearly states dull, matte, gray or grainy appearing solders are accpetable depending on your process and if the acceptability of the neaxt paragraph is met.IPC 610 and J-
Electronics Forum | Wed Oct 02 18:18:58 EDT 2002 | davef
The steadfast rule of thumb is: In order to get reliable reflow, you need to be at or higher than [liquidus + 20�C] for about 5 to 10 seconds, rather than those old "60 seconds above 183�C" guideline. This provides for setting your peak based on the
Electronics Forum | Thu Sep 26 11:44:23 EDT 2002 | abelardo
Hello everyone out there in the SMT world. I have a dilema I'm currently running a board that has 3 csp's with a .75 mm. ball pitch and .3mm ball size. And 2 qfp's-160. The stencil is 4 mils thick and I'm using a 63/37 solder paste. My reflow prof
Electronics Forum | Thu Sep 26 20:43:51 EDT 2002 | davef
"OK. If the connection doesn't look like I expect it to look, how do I know that the metallurgy is correct?" Comments are: * There are no pictures that will get you though this. * You should expect that gold that is dissolved in Pb/Sn solder to make
Electronics Forum | Fri Jan 18 12:34:14 EST 2013 | duchoang
Yes, I have. think I have pretty good reflow profile. We use Lead-Free,No-Clean,SAC305 Solder Paste. The problem is at LGA design.The pad size is alot bigger than BGA. They are totally flat and do not have balls/spheres which melted and collapsed thr
Electronics Forum | Thu Oct 31 09:34:38 EST 2002 | russ
We do this all of the time, This is what we do but I would be interested in other methods. 1. Remove component with BGA type rework station 2. Wick off lead pads only, verify/create even solder surface on the thermal pad on the board 3. Apply no-cle