Electronics Forum | Sun Jun 02 23:20:39 EDT 2002 | fastek
China is way behind the technology curve and will be for some time. They're still soaking up all of the through hole and 10 year old chipshooters they can get their hands on. China is the latest flavor of the month for cheap labor just like Mexico wa
Electronics Forum | Tue Jul 20 15:02:49 EDT 2010 | vetteboy86
I've seen this warp issue across several different PCB's we assemble. One of the biggest head ache's is getting the boards to transfer between machines, converyors, and inside our pick and place. Due to the warpage, transport between conveyors is dif
Electronics Forum | Thu Feb 24 00:06:00 EST 2000 | Ver Viray
Hi, Can anyone help me on how to choose profile points in wave soldering...e.g. smallest like R, C, to biggest like transformer heatsink etc.... Are the thermo-couples supposed to be on top of the pcb or at the bottom touching the solder bath when fl
Electronics Forum | Thu Feb 24 00:06:00 EST 2000 | Ver Viray
Hi, Can anyone help me on how to choose profile points in wave soldering...e.g. smallest like R, C, to biggest like transformer heatsink etc.... Are the thermo-couples supposed to be on top of the pcb or at the bottom touching the solder bath when fl
Electronics Forum | Mon Oct 18 22:15:11 EDT 2004 | KEN
I have two industry leading customers that have specific requirements for components to survive 30 seconds above 230C. In one case I have a custom ASIC that is heat sinked on the die (to the PCB). The sink pulls heat out of the lead frame very effi
Electronics Forum | Fri Feb 01 02:31:24 EST 2019 | sarason
You can buy an awful lot of PCB's with that budget. Having done multilayer at home for RF I would not recommend it. It took us 7 years to get a workable but I would not say reliable process running. 4 layer boards, plated through, green and silk scr
Electronics Forum | Mon Jan 18 10:01:16 EST 1999 | John W
| | | | Folk's, | | | | | | | | I'm looking for information of how long you cna store a gold finish PCB before building it. I know there are problems with the gold disappearing into the underlying nickle over time / temperature etc but exactly how l
Electronics Forum | Tue Jan 19 11:12:41 EST 1999 | Dave F
| | | | | Folk's, | | | | | | | | | | I'm looking for information of how long you cna store a gold finish PCB before building it. I know there are problems with the gold disappearing into the underlying nickle over time / temperature etc but exactly
Electronics Forum | Thu Mar 15 13:39:06 EDT 2018 | gregp
Impact is the instantaneous force at the time the component first reaches the PCB. F=M*a....so the acceleration is the key factor. If charted on a graph it would look like a spike...higher force for a short duration. The placement force is typical
Electronics Forum | Fri Aug 07 07:52:15 EDT 1998 | Earl Moon
| | Is there any problem using SMT on gold boards? 15 years ago we were told not to use gold boards, but I can't remember why. Judging by the other postings it now appears to be common. Only problem I see is that the nickel should be plated, not e
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830